The electrochemical properties of the organic radical battery (ORB) having a lithium metal anode and a cathode consisting of a nitroxide radical polymer poly(2,2,6,6-tetramethylpiperidinyloxy-4-yl methacrylate) (PTMA) with 1M LiPF 6 as an electrolyte in ethylene carbonate (EC)/dimethyl carbonate (DMC) have been evaluated at room temperature. The cell, with a thin cathode of 17 µm thickness incorporating 40 wt.% of PTMA, exhibited the full theoretical specific capacity at current densities up to 10 C (~1 mA/cm 2 ). However, a decrease in the specific capacity and an increase in the ohmic resistance were observed at higher current densities. The cell performance was good even on repeated charge-discharge cycles as an excess of 85 % retention of the initial discharge capacity was observed. This was true even after 400 cycles. However, a gradual decrease in capacity, an increase in charge-discharge voltage separation, and an electrode/electrolyte interfacial resistance have been observed after a large number of cycles. The examination of the scanning electron micrographs of the cathode material revealed that prolonged cycling resulted in the agglomeration of PTMA particles. These in turn increased the resistance and decreased the capacity of the cell.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.