The development of high-temperature heavy-duty turbine disk materials is critical for improving the overall efficiency of combined cycle power plants. An alloy development strategy to this end involves superalloys strengthened by ‘compact’ γ′-γ″ coprecipitates. Compact morphology of coprecipitates consists of a cuboidal γ′ precipitate such that γ″ discs coat its six {001} faces. The present work is an attempt to investigate the microstructure and creep behavior of a fully aged alloy exhibiting compact coprecipitates. We conducted heat treatments, detailed microstructural characterization, and creep testing at 1200 °F (649 °C) on an IN718-variant alloy. Our results indicate that aged IN718-27 samples exhibit a relatively uniform distribution of compact coprecipitates, irrespective of the cooling rate. However, the alloy ruptured at low strains during creep tests at 1200 °F (649 °C). At 100 ksi (689 MPa) load, the alloy fails around 0.1% strain, and 75 ksi (517 MPa) loading causes rupture at 0.3% strain. We also report extensive intergranular failure in all the tested samples, which is attributed to cracking along grain boundary precipitates. The results suggest that while the compact coprecipitates are indeed thermally stable during thermomechanical processing, the microstructure of the alloy needs to be optimized for better creep strength and rupture life.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.