Multi layered lightweight material compounds such as hybrid laminates are composed of different layers of materials like metals and unidirectional fibre-reinforced plastics and offer high specific strength. They can be individually tailored for applications like outer cover panels for aircraft and vehicles. Many characteristics especially layer structure, volume contents of the embedded materials as well as layer surface adhesion determine the performance of a hybrid laminate. In this study, the influence of layer structure and metal volume content are evaluated with regard to the mechanical properties of the recyclable hybrid laminate CAPAAL (carbon fibre-reinforced plastics/aluminium foil laminate), which consists of the aluminium alloy AA6082 and a graded structure of glass and carbon fibre-reinforced polyamide 6. Hybrid laminates with different ratios of the fibre-reinforced plastic and numbers of aluminium layers were manufactured by thermal pressing. The consolidation quality of in total four laminate structure variations, including 2/1 and 3/2 metal-to-fibre-reinforced plastic layer structures with fibre orientation variation, were investigated by light microscopy through cross-sections and further on computed tomography. For determination and evaluation of the mechanical properties metrologically instrumented quasi-static tensile and three-point bending tests, as well as tension-tension fatigue tests for the establishment of S-N curves were performed. The results were correlated to the microstructural observations, revealing significant influence by the consolidation quality. The layer structure proved to have a proportional impact on the increase of quasi-static tensile and flexure strength with a decrease in metal volume content. Orienting some of the fibre-reinforced plastic layers in ±45° leads to a more evenly distributed fibre alignment, which results in a higher consolidation quality and less anisotropic bending properties. Fatigue results showed a more complex behaviour where not only the metal volume content seems to determine the fatigue loading capability, but also the number of metal-fibre-reinforced plastic interfaces, hinting at the importance of stress distribution between layers and its longevity over fatigue life.
Short glass fiber reinforced plastics (SGFRP) offer superior mechanical properties compared to polymers, while still also enabling almost unlimited geometric variations of components at large-scale production. PA6-GF30 represents one of the most used SGFRP for series components, but the impact of injection molding process parameters on the fatigue properties is still insufficiently investigated. In this study, various injection molding parameter configurations were investigated on PA6-GF30. To take the significant frequency dependency into account, tension–tension fatigue tests were performed using multiple amplitude tests, considering surface temperature-adjusted frequency to limit self-heating. The frequency adjustment leads to shorter testing durations as well as up to 20% higher lifetime under fatigue loading. A higher melt temperature and volume flow rate during injection molding lead to an increase of 16% regarding fatigue life. In situ Xray microtomography analysis revealed that this result was attributed to a stronger fiber alignment with larger fiber lengths in the flow direction. Using digital volume correlation, differences of up to 100% in local strain values at the same stress level for different injection molding process parameters were identified. The results prove that the injection molding parameters have a high influence on the fatigue properties and thus offer a large optimization potential, e.g., with regard to the component design.
Combining carbon fiber reinforced polymers (CFRP) with steel offers the potential of utilizing the desired characteristics of both materials, such as specific strength/stiffness and fatigue strength of fiber reinforced polymers (FRP) and impact resistance of metals. Since in such hybrid laminates multiple material layers are combined, a gradual failure is likely that can lead to changes in mechanical properties. A failure of the metal partner leads to an increase in stress on the FRP, which under fatigue load results in increased self-heating of the FRP. Therefore, a suitable testing procedure is required and developed in this study, to enable a reproducible characterization of the mechanical properties under fatigue load. The resulting testing procedure, containing multiple frequency tests as well as load increase and constant amplitude tests, enabled characterization of the fatigue performance while never exceeding a testing induced change in temperature of 4 K. In addition to the development of the testing procedure, an insight into the manufacturing induced residual stresses occurring in such hybrid laminates, which impacts the load-bearing capacity, was established using finite element simulation. The gathered data and knowledge represents a basis for future in-depth investigations in the area of residual stress influence on the performance of hybrid laminates and highlights its importance, since not only the used testing procedure determines the measured fatigue performance.
Nano-reinforcements in carbon fibre-reinforced polymer (CFRP) have proven to enhance the mechanical properties considering quasi-static, as well as fatigue load and, are a promising option with regard to CFRP performance optimisation. While general knowledge about the nanofiller content and its influence in CFRP is well documented, the use of alignment techniques for a specific orientation of the nano-reinforcements is still insufficiently studied. In this work, the influence of oriented carbon nanofibres (CNF) on the mechanical properties of bidirectional CFRP is investigated. CFRP was produced CNF-reinforced with and without orientation using a hot press, where an electric field was applied during curing. The laminates were characterised with respect to dispersion quality, pore volume, quasi-static properties (tensile and bending tests) and dynamic properties (fatigue tests). Electrical resistance measurement was applied together with digital image correlation and in situ computed tomography to generate knowledge about the fatigue-related damage evolution and evaluate the sensors for viable use of condition monitoring. Results show that the orientation of CNF has a significant impact on both quasi-static and fatigue properties, increasing the strength while reducing and slowing down the introduced damage. Orientation of nanofillers thus shows large optimization potential of mechanical properties of CFRP components.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.