Lead halide perovskite solar cells have significantly increased in both efficiency and stability over the last decade. An important aspect of their long-term stability is the reaction between the perovskite and other materials in the solar cell. This includes the contact materials and their degradation if they can potentially come into contact through, e.g., pinholes or material diffusion and migration. Here, we explore the interactions of silver contacts with lead halide perovskites of different compositions by using a model system where thermally evaporated silver was deposited directly on the surface of the perovskites. Using X-ray photoelectron spectroscopy with support from scanning electron microscopy, X-ray diffraction, and UV–visible absorption spectroscopy, we studied the film formation and degradation of silver on perovskites with different compositions. The deposited silver does not form a continuous silver film but instead tends to form particles on a bare perovskite surface. These particles are initially metallic in character but degrade into AgI and AgBr over time. The degradation and migration appear unaffected by the replacement of methylammonium with cesium but are significantly slowed down by the complete replacement of iodide with bromide. The direct contact between silver and the perovskite also significantly accelerates the degradation of the perovskite, with a significant loss of organic cations and the possible formation of PbO, and, at the same time, changed the surface morphology of the iodide-rich perovskite interface. Our results further indicate that an important degradation pathway occurred through gas-phase perovskite degradation products. This highlights the importance of control over the interface materials and the use of completely hermetical barrier layers for the long-term stability and therefore the commercial viability of silver electrodes.

Metal halide perovskites have emerged as materials of high interest for solar energy-to-electricity conversion, and in particular, the use of mixed-ion structures has led to high power conversion efficiencies and improved stability. For this reason, it is important to develop means to obtain atomic level understanding of the photoinduced behavior of these materials including processes such as photoinduced phase separation and ion migration. In this paper, we implement a new methodology combining visible laser illumination of a mixed-ion perovskite ((FAPbI3)0.85(MAPbBr3)0.15) with the element specificity and chemical sensitivity of core-level photoelectron spectroscopy. By carrying out measurements at a synchrotron beamline optimized for low X-ray fluxes, we are able to avoid sample changes due to X-ray illumination and are therefore able to monitor what sample changes are induced by visible illumination only. We find that laser illumination causes partially reversible chemistry in the surface region, including enrichment of bromide at the surface, which could be related to a phase separation into bromide- and iodide-rich phases. We also observe a partially reversible formation of metallic lead in the perovskite structure. These processes occur on the time scale of minutes during illumination. The presented methodology has a large potential for understanding light-induced chemistry in photoactive materials and could specifically be extended to systematically study the impact of morphology and composition on the photostability of metal halide perovskites.

A trend in high performing lead halide perovskite solar cell devices has been increasing compositional complexity by successively introducing more elements, dopants, and additives into the structure; and some of the latest top efficiencies have been achieved with a quadruple cation mixed halide perovskite Cs x FA y MA z Rb 1-x-y-z PbBr q I 3-q . This paper continues this trend by exploring doping of mixed lead halide perovskites, FA 0.83 MA 0.17 PbBr 0.51 I 2.49 , with an extended set of alkali cations, i.e., Cs + , Rb + , K + , and Na + , as well as combinations of them. The doped perovskites were investigated with X-ray diffraction, energy-dispersive X-ray spectroscopy, scanning electron microscopy, hard X-ray photoelectron spectroscopy, UV−vis, steady state fluorescence, and ultrafast transient absorption spectroscopy. Solar cell devices were made as well. Cs + can replace the organic cations in the perovskite structure, but Rb + , K + , and Na + do not appear to do that. Despite this, samples doped with K and Na have substantially longer fluorescence lifetimes, which potentially could be beneficial for device performance.

Lead halide perovskites have become a leading material in the field of emerging photovoltaics and optoelectronics. Significant progress has been achieved in improving the intrinsic properties and environmental stability of...

Surface properties of colloidal quantum dots (CQDs) are critical for the transportation and recombination of the photoinduced charge carrier in CQD solar cells, therefore dominating the photovoltaic performance. Herein, PbS CQD passivated using liquid-state ligand exchange (LSLX) and solid-state ligand exchange (SSLX) strategies are in detail investigated using photoelectron spectroscopy (PES), and solar cell devices are prepared to understand the link between the CQD surface properties and the solar cell function. PES using different energies in the soft and hard Xray regime is applied to study the surface and bulk properties of the CQDs, and the results show more effective surface passivation of the CQDs prepared with the LSLX strategy and less formation of lead-oxide. The CQD solar cells prepared with LSLX strategy show higher performance, and the photoelectric measurements suggest that the recombination of photoinduced charges is reduced for the solar cell prepared with the LSLX approach. Meanwhile, the fabricated solar cells exhibit good stability. This work provides important insights into how to fine-tune the CQD surface properties by improving the CQD passivation, and how this is linked to further improvements of the device photovoltaic performance.

Scalable methods for deposition of lead halide perovskite thin films are required to enable commercialization of the highly promising perovskite photovoltaics. Here, we have developed a slot-die coating process under ambient conditions for methylammonium lead iodide (MAPbI 3 ) perovskite on heated substrates (about 90 °C on the substrate surface). Dense, highly crystalline perovskite films with large grains (100–200 μm) were obtained by careful adjustment of the deposition parameters, using solutions that are similar but more dilute than those used in typical spin-coating procedures. Without any further after treatments, such as antisolvent treatment or vapor annealing, we achieved power conversion efficiencies up of 14.5% for devices with the following structure: conducting tin oxide glass (FTO)/TiO 2 /MAPbI 3 /spiro-MeOTAD/Au. The performance was limited by the significant roughness of the deposited films, resulting from the hot-casting method, and the relatively high deposition temperature, which led to a defect-rich surface due to loss of MAI.

No abstract

CsyFA1−yPb(IxBr1−x)3 perovskite solar cells were prepared using non-hazardous solvents and metallic nitrate precursor films for the material synthesis.