New, water soluble poly(glycidol) (PGl) macroinitiators for atom transfer radical polymerization (ATRP) were synthesized. This new class of macroinitiators were prepared in a three‐step process. First, series of well‐defined ω‐hydroxyl functional poly(glycidol acetal)s with different molecular weights was synthesized via anionic polymerization followed by quantitative termination of anionically growing active sites. End capping was achieved by treatment of living chain ends with water. The living nature of the system and termination reaction is discussed. In the second stage, monofunctional poly(glycidol acetal)s were functionalized by esterification with 2‐chloropropionyl chloride. Finally, selective deprotection (hydrolysis) of acetal protective groups was performed. As simultaneous partial cleavage of ester bond of attached ATRP moieties was unavoidable, the final functionality of macroinitiator calculated from 1H NMR varied in the range 85–95%. The obtained (2‐chloropropionyl) poly(glycidol) macroinitiator with DP = 55 and 90% functionality was successfully used in ATRP polymerization of N‐isopropylacrylamide (NIPAAm) at room temperature in the DMF/water mixture. Linear block copolymers with relatively narrow molecular weight distribution and controlled composition were obtained and characterized with 1H NMR and SEC‐MALLS measurements. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 2488–2499, 2008

Block copolymers of poly(glycidol)‐b‐poly(4‐vinylpyridine) were obtained by ATRP of 4‐vinylpyridine initiated by ω‐(2‐chloropropionyl) poly(glycidol) macroinitiators. By changing the monomer/macroinitiator ratio in the synthesis polymers with varied P4VP/PGl molar ratio were obtained. The obtained block copolymers showed pH sensitive solubility. It was found that the linkage of a hydrophilic poly(glycidol) block to a P4VP influenced the pKa value of P4VP. DLS measurements showed the formation of fully collapsed aggregates exceeding pH 4.7. Above this pH values the collapsed P4VP core of the aggregates was stabilized by a surrounding hydrophilic poly(glycidol) corona. The size of the aggregates depended significantly upon the composition of the block copolymers. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 1782–1794, 2009

Summary: The synthesis and polymerization of macromonomers containing a polymerizable styrene head group and a tail of ethylene oxide derivatives of different character were investigated. The synthesis of macromonomers was based on living anionic polymerization of oxiranes. Two monomers were used: 1‐ethoxyethyl glycidyl ether (glycidol acetal), which after hydrolysis forms hydrophilic glycidol blocks and glycidyl phenyl ether forming hydrophobic blocks. Polymerizable double bonds were introduced by terminating the living chain with p‐(chloromethyl)styrene. The radical polymerization of the macromonomers was carried out in water with addition of a non‐polar solvent (benzene) and AIBN as initiator. Core‐shell polymers of different character and molar masses were obtained. The conversion of polymerized macromonomers was around 50%. However, the polymerization product could easily be separated from the reaction mixture. magnified image