This study investigated the sonication effect on the mechanical properties of thermoplastic natural rubber (TPNR) nanocomposites reinforced by multi-walled carbon nanotubes (MWCNTs). The TPNR nanocomposites were prepared using the melt blending method from polypropylene, natural rubber and liquid natural rubber as a compatibilizer, respectively, with 1% of MWCNTs. The results showed that a good dispersion on nanotubes was achieved by sonication. An optimal sonication time of 1 h was found to produce nanocomposites with maximum tensile and impact strength. The Young’s modulus, tensile strength, elongation at break and impact strength increased by almost 11%, 21%, 43% and 50%, respectively as compared with a pristine TPNR sample. The effect of sonication was also confirmed by dynamic mechanical analysis, it showed that the storage modulus E′, loss modulus E″ and glass transition temperature ( Tg) also increased for all MWCNTs reinforced samples. Scanning electron micrographs confirm the effect of good dispersion of MWCNTs and their interfacial bonding in TPNR after sonication.
This study investigated the mechanical properties of thermoplastic natural rubber (TPNR) nanocomposites reinforced by multi-walled carbon nanotubes (MWNTs). The TPNR nanocomposites were prepared using melt blending method from polypropylene, natural rubber, and liquid natural rubber as a compatibilizer, respectively, with 1—7 wt% of MWNTs. The tensile strength and Young’s modulus increased by almost 39% and 30%, respectively, at 3 wt% of MWNTs. The elongation at break decreased with increase in the percentage of MWNTs. The maximum impact strength was recorded at 5 wt% of MWNTs which was increased by 74% as compared with a pristine TPNR sample. The effect of MWNTs was also confirmed by DMA; it showed that the storage modulus E′, loss modulus E′′, and glass transition temperature (Tg) also increased for all MWNT reinforced samples. SEM micrographs confirm the effect of good dispersion of MWNTs and their interfacial bonding in TPNR.
This article studies the thermal properties of a multi-walled carbon nanotube (MWNT)-reinforced thermoplastic natural rubber (TPNR) nanocomposite. The nanocomposite was prepared using a melt blending method. Various percentages (1, 3, 5, and 7 wt%) of MWNTs were added into TPNR to improve its thermal properties. The laser flash technique was also employed to determine the thermal conductivity, thermal diffusivity, and specific heat capacity of the nanocomposite. The DMA result showed that the glass transition temperature (Tg) increased with the increase in MWNT content. TEM micrographs also demonstrated that a good dispersion of MWNTs was achieved in the TPNR environment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.