ABSTRACT:Terpolymer syrups were photopolymerized from 2-ethylhexyl acrylate, 2-hydroxylethyl acrylate and isobornyl acrylate to prepare acrylic pressure sensitive adhesives (PSAs). After polymerization, various crosslinkers as 1,6-hexanediol diacrylate (HDDA), poly (ethylene glycol) diacrylate (PEGDA, Mn = 250, 575, and 700) were added and then UV-irradiated to prepare the semi-IPN type PSAs. Their adhesion performance and storage modulus (G') were strongly dependent on their chemical structure and molecular weight of the crosslinkers. Optical properties such as transmittance (> 92.5 %), haze (< 1.0 %) and color-difference (< 0.3) of PSAs samples were not affected by crosslinker types used in this study.
Transparent acrylic pressure sensitive adhesives (PSAs) were successfully prepared by photopolymerization with 2-ethylhexyl acrylate (2-EHA) and 2-hydroxyethyl acrylate (2-HEA) as a default constituent and with isobornyl acrylate (IBOA) and N-(isobutoxymethyl)acrylamide (IBMA) as a variable constituent. The IBMA mole fraction effect in the acrylic PSAs was investigated on adhesion performances and the optical properties including 85/85 test as well as the characteristics (solid content, and molecular weight) of the PSA syrups were also investigated. Regardless increasing the IBMA mole fraction in the acrylic PSAs, the acrylic PSAs exhibited almost the same adhesion performance such as 180 o peel strength (~4.0 kg/25 mm) and probe tack (~0.27 kg). All the acrylic PSA samples also showed high transmittance (more than 91%), low haze (less than 1.0%) and low color-difference (less than 1.0) before and after 85/85 test.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.