This in vitro study aims to evaluate whether a solution of 10% sodium ascorbate (SA) may exert a beneficial effect on the bonding of composite to enamel after using different bleaching agents and protocols. Microtensile bond strength (µTBS) was evaluated on 72 freshly extracted human central incisors, divided into eight experimental groups and one control group (total n = 9): Group 1 serves as control (nonbleached). Group 2 was bleached with 5% carbamide peroxide. Group 3 was bleached with 5% carbamide peroxide and then treated with 10% SA. Group 4 was bleached with 10% carbamide peroxide. Group 5 was bleached with 10% carbamide peroxide, then treated with 10% SA. Group 6 was bleached with 16% carbamide peroxide. Group 7 was bleached with 16% carbamide peroxide, then treated with 10% SA. Group 8 was bleached with 6% hydrogen peroxide. Group 9 was bleached with 6% hydrogen peroxide, then treated with 10% SA. All groups were restored immediately after the different treatments using a resin composite. The µTBS values were measured using a universal testing machine and statistical analysis was performed by means of normality and variance analyses, SIDAK test for univariate test and multiple comparisons, and Student test to compare µTBS values of each group with the control. The mean µTBS values in groups 2, 4, 6, 8 were significantly lower than controls. For groups 3, 5, 7, 9, subjected to antioxidant (10% SA) application, all µTBS values increased significantly. However, only for Groups 3 and 5 there was no significant difference with the control. Applying 10% SA for 10 min may improve the bond strength composite/bleached enamel just when whitening is performed with 5% and 10% carbamide peroxide.

The aim of this study was to assess the one year clinical performance of a new application method, the Fast-Modelling Bulk Technique (FMBT), in comparison to the Composite-Up Layering Technique (CULT) in posterior cavities. Thirty patients with two class I cavities on permanent human molars were enrolled in the present study. A total of sixty class I cavities were prepared and randomly divided according to the restoration technique used: 30 cavities restored by incremental layering technique and modelling of the last layer with Composite-Up Technique (CUT) using the composite Filtek Z250XT (3M ESPE; St. Paul, MN, USA) and the other 30 restored by Bulk Filling technique and modelling of the last layer by Fast-Modelling Technique (FMT) using the composite Filtek Bulk Fill Posterior Restorative (3M ESPE; St. Paul, MN, USA). Restorations were evaluated for up to one year by two observers according to Federation Dentaire Internationale (FDI) criteria, through clinical and radiological exams. Exact Fisher tests were used for statistical analysis. (p ≤ 0.05). From a biological perspective, at baseline, teeth restored with both techniques did not reveal any postoperative sensitivity. However, with time, FMBT showed less postoperative sensitivity and therefore more desirable results than CULT with a nonsignificant difference after one year (p > 0.05). Concerning secondary caries, fracture of the material, and marginal adaptation, no significant difference was noted between both techniques (p > 0.05). Regarding marginal staining, CULT resulted in more staining with a significant difference, as compared to FMBT (p < 0.05). Upon radiological examination, FMBT showed a good marginal fit during the first year, whereas CULT showed small empty voids from baseline with a nonsignificant difference (p = 1.00). After one year of clinical function, both techniques showed promising results. The present study indicates that the new FMBT could have a positive effect on the marginal staining of resin composite.

This study investigated the effect of intraoral humidity on microtensile bond strength (μTBS) to dentin of two universal adhesives applied in self-etch (SE) mode. Forty extracted human molars were selected for this study. Dentin specimens were allocated into four groups, standardized and then bonded with two commercial multimode adhesives, according to two humidity conditions (50% relative humidity (RH) and 90% RH). Following composite resin build-up and 24 h of water storage, the μTBS of the bonded interface was analyzed. The 50% RH was higher for Scotchbond Universal (SBU) than Prime&Bond Universal (PBU), while for 90% RH, SBU had significantly lower values than PBU. With PBU, the mean bond strength was not significantly different between both humidity settings tested (p > 0.05), while for SBU, the mean bond strength was significantly different between both conditions tested (p < 0.05); μTBS was significantly higher for 50% RH than for the other group. Within the limitation of this in vitro study, it can be concluded that: 1) the bonding performance of adhesives systems depends on the humidity settings; 2) increased RH exerts a detrimental effect on the bond strength of 2-hydroxyethyl methacrylate (HEMA)-containing adhesive tested. However, this phenomenon was not observed for HEMA-free adhesive tested; 3) further research in this area is needed to investigate different adhesive systems, temperatures and humidity settings.

No abstract