Recently, amorphous/disordered oxide thin films made from Fe and lanthanides like Dy and Tb have been reported to have a rich set of magnetic, optical, and electronic properties, as well as room-temperature magneto-electric coupling with multiferroics [A. Malasi et al., Sci. Rep. 5, 18157 (2015); H. Taz et al., Sci. Rep. 6, 27869 (2016); and H. Taz et al., Sci. Rep. 10, 1–10 (2020)]. Here, we report the synthesis and detailed characterization of Fe2.75Dy-oxide thin films prepared on various substrates using electron beam co-evaporation. The structure, chemistry, electric, magnetic, and optical properties were studied for the as-prepared and annealed (373 K, in air, 1 h) films of thickness 40 nm. High resolution transmission electron microscopy and electron diffraction study showed that the films were amorphous in both the as-prepared and annealed states. The electron energy-loss spectroscopy studies quantified that metal oxygen stoichiometry changed from Fe2.75Dy-O1.5 to Fe2.75Dy-O1.7 upon annealing. Synchrotron-based x-ray absorption spectroscopy investigation confirmed that the as-prepared films were highly disordered with predominantly metallic Fe and Dy states that became slightly oxidized with annealing in air. The as-prepared amorphous films demonstrated significantly high value of ordinary (∼10 cm2/V s) and anomalous (∼102 cm2/V s) Hall mobility and high electrical conductivity of ∼103 S/cm at room temperature. The cryogenic magnetic property measurement shows two-step magnetization below 200 K, suggesting exchange-spring magnetic interaction. The nature of the field cooled and zero-field cooled curves suggested a spin-glass like transition between 78 K and 80 K, with a characteristic broad peak. The Tauc plot analysis from optical transmission spectra confirms the existence of an optical bandgap of ∼2.42 eV that increased slightly to ∼2.48 eV upon annealing. This rich set of transport, optical, and magnetic properties in these thin films is very exciting and points to potential applicability in low-cost multifunctional devices requiring a combination of transparent, semiconducting, and magnetic responses, such as in spintronics.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.