Composite materials were prepared by mixing fly ash obtained from biomass combustion as filler and isotactic polypropylene (PP) as matrix. Three silane‐type coupling agents mainly differing in the size of their functional groups were used to improve the compatibility between both components. Uniaxial tensile tests showed that the incorporation of untreated ash into PP led to stiffer but also more brittle and weaker materials, as Young's modulus significantly increased and tensile strength and elongation at break decreased. Furthermore, an enhancement in storage and loss moduli as well as in composite viscosity was observed with the addition of fly ash. Hardness tests and thermal and fracture surface analyzes revealed tensile test results similar to those mentioned earlier. In summary, after analyzing the effects of the three silanes on mechanical, thermal, morphological, and rheological properties, the silane containing the vinyl functional group (XL10) was selected as the most appropriate for the PP/ash composites investigated. POLYM. COMPOS., 31:1722–1730, 2010. © 2010 Society of Plastics Engineers.

No abstract

No abstract

No abstract

No abstract

No abstract

The effect of different toughening strategies on the mechanical properties of multiwalled carbon nanotube/polycarbonate composite (PC/MWNT) for electromagnetic interference shielding was analyzed from the mechanical and fracture tests using linear elastic fracture mechanics. The effect of processing (injection and compression molding) and manufacturing (annealing) conditions in the mechanical properties and electrical conductivity has been studied. The classic electromagnetic theory predicts a shielding effectiveness around 40 dB for nanocomposites with 5 wt% of MWNT in the frequency range studied. These values make these compounds to be very interesting materials for potential applications as electronic housings. Therefore, a combination of cyclic form of polybutylene terephthalate addition and annealing strategies let to optimize flexural parameters and improve the flexural modulus of PC composites. The rheology results showed that the dynamic moduli and the viscosity grew with increasing MWNT content. A significant change in frequency dependence of the moduli was observed, with respect to pure PC, which indicates a transition from a liquid‐like to a solid‐like behavior. Finally, the morphological study proves that the composites display different toughening mechanisms as function of carbon nanotube quantity. This fact could explain the different fracture behaviors of materials. In summary, it has been proved that it is possible to obtain PC/MWNT nanocomposites with relatively high conductivity, minimizing the loss of mechanical properties, using processing techniques easily scalable at industrial level. POLYM. COMPOS., 34:1938–1949, 2013. © 2013 Society of Plastics Engineers

Woodflour/polypropylene composites were prepared with 10 and 20% in weight of woodflour (WF). The influence of the WF, the compatibilizer, and processing aid (WP) in the crystalline structure of the polypropylene was studied by thermal analysis. The results showed that the WF acts as a nucleating agent, increasing the crystallization rate of the PP at the cooling rates studied. The morphological study by SEM proved that the WP increased the dispersion of the filler into the PP matrix, and the ionomer, used like compatibilized improved the adhesion between the PP and the filler obtaining a more uniform morphology. The mechanical properties indicated that the incorporation of the ionomer and the WP enhanced the ductility of the composites at the same time that the materials reached a more uniform morphology. The amount of additives (compatibilizer and WP) included in the woodflourplastic composite (WPC) formulations was small, for this, the formulations are suitable to use in a possible industrial application.