We engineered functional cardiac patches by seeding neonatal rat cardiomyocytes onto carbon nanotube (CNT) incorporated photocrosslinkable gelatin methacrylate (GelMA) hydrogel. The resulting cardiac constructs showed excellent mechanical integrity and advanced electrophysiological functions. Specifically, myocardial tissues cultured on 50 μm thick CNT-GelMA showed 3 times higher spontaneous synchronous beating rates and 85% lower excitation threshold, compared to those cultured on pristine GelMA hydrogels. Our results indicate that the electrically conductive and nanofibrous networks formed by CNTs within a porous gelatin framework is the key characteristics of CNT-GelMA leading to improved cardiac cell adhesion, organization, and cell-cell coupling. Centimeter-scale patches were released from glass substrates to form 3D biohybrid actuators, which showed controllable linear cyclic contraction/extension, pumping, and swimming actuations. In addition, we demonstrate for the first time that cardiac tissues cultured on CNT-GelMA resist damage by a model cardiac inhibitor as well as a cytotoxic compound. Therefore, incorporation of CNTs into gelatin, and potentially other biomaterials, could be useful in creating multifunctional cardiac scaffolds for both therapeutic purposes and in vitro studies. These hybrid materials could also be used for neuron and other muscle cells to create tissue constructs with improved organization, electroactivity, and mechanical integrity.

Thin‐film solar cells are made by vapor deposition of Earth‐abundant materials: tin, zinc, oxygen and sulfur. These solar cells had previously achieved an efficiency of about 2%, less than 1/10 of their theoretical potential. Loss mechanisms are systematically investigated and mitigated in solar cells based on p‐type tin monosulfide, SnS, absorber layers combined with n‐type zinc oxysulfide, Zn(O,S) layers that selectively transmit electrons, but block holes. Recombination at grain boundaries is reduced by annealing the SnS films in H2S to form larger grains with fewer grain boundaries. Recombination near the p‐SnS/n‐Zn(O,S) junction is reduced by inserting a few monolayers of SnO2 between these layers. Recombination at the junction is also reduced by adjusting the conduction band offset by tuning the composition of the Zn(O,S), and by reducing its free electron concentration with nitrogen doping. The resulting cells have an efficiency over 4.4%, which is more than twice as large as the highest efficiency obtained previously by solar cells using SnS absorber layers.

SnS is a promising earth-abundant material for photovoltaic applications. Heterojuction solar cells were made by vapor deposition of p-type tin(II) sulfide, SnS, and n-type zinc oxysulfide, Zn(O,S), using a device structure of soda-lime glass/Mo/SnS/Zn(O,S)/ZnO/ITO. A record efficiency was achieved for SnS-based thin-film solar cells by varying the oxygen-to-sulfur ratio in Zn(O,S). Increasing the sulfur content in Zn(O,S) raises the conduction band offset between Zn(O,S) and SnS to an optimum slightly positive value. A record SnS/Zn(O,S) solar cell with a S/Zn ratio of 0.37 exhibits short circuit current density (Jsc), open circuit voltage (Voc), and fill factor (FF) of 19.4 mA/cm2, 0.244 V, and 42.97%, respectively, as well as an NREL-certified total-area power-conversion efficiency of 2.04% and an uncertified active-area efficiency of 2.46%.

Air-stable dimers of sandwich compounds including rhodocene and (pentamethylcyclopentadienyl)(arene)ruthenium and iron derivatives can be used for n-doping electron-transport materials with electron affinities as small as 2.8 eV. A p-i-n homojunction diode based on copper phthalocyanine and using rhodocene dimer as n-dopant shows a rectification ratio of greater than 10(6) at 4 V.