The Pt‐Sn/CNDs electrocatalyst was synthesized by the alcohol reduction method with the aim to reduce platinum loading and improve electroactivity. XPS results showed that the nanoparticles were present in the form of Pt‐Sn metallic alloy with a significant amount of SnO‐ species which facilitate the rapid oxidation of CO intermediates. The lattice parameter of Pt in Pt‐Sn/CNDs electrocatalyst was calculated to be 0.3926 nm; this value is higher than 0.3921 nm, the lattice parameter of Pt in Pt/CNDs electrocatalyst. XRD results proved that incorporating tin (Sn) into the Pt/CNDs electrocatalyst modifies the face centred cubic shape of platinum to a crystalline structure which improves the alcohol electro‐oxidation reactions. The electrochemical tests proved that the Pt‐Sn/CNDs electrocatalyst exhibited high current densities and lower poisoning rates compared to the Pt/CNDs and Pt/C electrocatalysts. The Pt‐Sn/CNDs electrocatalyst showed the greatest electroactivity for both methanol and ethanol electro‐oxidation reactions.
Carbon nano-onions (CNOs) were successfully synthesized by employing the flame pyrolysis (FP) method, using flaxseed oil as a carbon source. The alcohol reduction method was used to prepare Pd/CNOs and Pd-Sn/CNOs electro-catalysts, with ethylene glycol as the solvent and reduction agent. The metal-nanoparticles were supported on the CNO surface without adjusting the pH of the solution. High-resolution transmission electron microscopy (HRTEM) images reveal CNOs with concentric graphite ring morphology, and also PdSn nanoparticles supported on the CNOs. X-ray diffractometry (XRD) patterns confirm that CNOs are amorphous and show the characteristic diffraction peaks of Pd. There is a shifting of Pd diffraction peaks to lower angles upon the addition of Sn compared to Pd/CNOs. X-ray photoelectron spectroscopy (XPS) results also confirm the doping of Pd with Sn to form a PdSn alloy. Fourier transform infrared spectroscopy (FTIR) displays oxygen, hydroxyl, carboxyl, and carbonyl, which facilitates the dispersion of Pd and Sn nanoparticles. Raman spectrum displays two prominent peaks of carbonaceous materials which correspond to the D and G bands. The Pd-Sn/CNOs electro-catalyst demonstrates improved electro-oxidation of methanol and ethanol performance compared to Pd/CNOs and commercial Pd/C electro-catalysts under alkaline conditions.
Carbon nanodots (CNDs) were successfully synthesized employing a cheap and green method using oats as a starting material. The Pt/CNDs electrocatalyst was synthesized using carbon nanodots as a reductant and support material without adjusting the pH of the solution. The synthesized materials were characterized using Fourier transform infrared spectroscopy (FTIR), Brunauer-Emmett-Teller Nitrogen adsorption (BET), X-ray photoelectron spectroscopy (XPS), Transmission electron microscopy (TEM), X-ray diffractometry (XRD) and Inductively coupled plasma optical emission spectroscopy (ICP-OES). The FTIR results proved that the synthesized carbon nanodots contain carboxylic acid functional groups which facilitate the attachment of Pt nanoparticles. The BET surface area for carbon nanodots was found to be 312.5 m 2 g -1 two times higher than that of commercial carbon. XPS results revealed the composition of the materials and the oxidation states of Pt in Pt/CNDs electrocatalyst. TEM images proved that the materials were of the nanoscale. XRD peaks proved that the carbon nanodots were amorphous and Pt (111) was present in the Pt/CNDs electrocatalyst. ICP-OES determined the platinum concentration in Pt/CNDs electrocatalyst to be 8.12%. The electrochemical oxidation of methanol and ethanol were studied by cyclic voltammetry (CV) and chronoamperometry (CA). Cyclic voltammetry results showed that the Pt/CNDs electrocatalyst prepared by this method exhibit superior performance for methanol and ethanol electro-oxidation at room temperature.
Mn-doped spinel oxides MnxNi1−xCo2O4 (x = 0, 0.3, 0.5, 0.7, and 1) were synthesized using the citric acid-assisted sol–gel method. The Mn0.5Ni0.5Co2O4 (x = 0.5) supported on carbon nanosheets, Mn0.5Ni0.5Co2O4/C, was also prepared using the same method employing NaCl and glucose as a template and carbon source, respectively, followed by pyrolysis under an inert atmosphere. The electrocatalytic oxygen reduction reaction (ORR) activity was performed in alkaline media. Cyclic voltammetry (CV) was used to investigate the oxygen reduction performance of MnxNi1−xCo2O4 (x = 0, 0.3, 0.5, 0.7, and 1), and Mn0.5Ni0.5Co2O4 was found to be the best-performing electrocatalyst. Upon supporting the Mn0.5Ni0.5Co2O4 on a carbon sheet, the electrocatalytic activity was significantly enhanced owing to its large surface area and the improved charge transfer brought about by the carbon support. Rotating disk electrode studies show that the ORR electrocatalytic activity of Mn0.5Ni0.5Co2O4/C proceeds via a four-electron pathway. Mn0.5Ni0.5Co2O4/C was found to possess E1/2(V) = 0.856, a current density of 5.54 mA cm−2, and a current loss of approximately 0.11% after 405 voltammetric scan cycles. This study suggests that the interesting electrocatalytic performance of multimetallic transition metal oxides can be further enhanced by supporting them on conductive carbon materials, which improve charge transfer and provide a more active surface area.
Palladium-based catalysts serve as promising electrocatalysts for the oxidation of ethylene glycol to produce electrical energy that can be used to address the continuous worldwide energy demand increments along with the depletion of fossil fuels which serve as the main energy source. For optimal catalysts performance, carbon nanotubes and carbon nanodots were investigated as palladium catalyst support materials to address difficulties in oxidizing and breaking the C–C bonds in ethylene glycol, cost of electrocatalyst, and complex reaction mechanism that is restraining rapid development and applications of direct ethylene glycol fuel cells (DEGFC). Utilization of palladium catalysts supported on carbon nanotubes (CNT) and carbon nanodots (CND) as support materials resulted in spontaneous ethylene glycol oxidation. The Pd/CNT catalyst showed greater stability compared to Pd/CND during the oxidation of ethylene glycol, and it is not easily poisoned by carbon monoxide intermediates formed during ethylene glycol oxidation as shown by a slow current decay on chronoamperometry.
Carbon nanofibers (CNFs) supported by Pd and Pd-Sn electro-catalysts were prepared by the chemical reduction method using ethylene glycol as the reducing agent. Their physicochemical characteristics were studied using high resolution-transmission electron microscopy (HR-TEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA) and Bruanaer-Emmett-Teller (BET) analysis. FTIR revealed that oxygen, hydroxyl, carboxylic and carbonyl functional groups facilitated the dispersion of Pd and Sn nanoparticles. The doping of Pd with Sn to generate PdSn alloy was also confirmed by XPS data. The amorphous nature of CNFs was confirmed by XRD patterns which exhibited the Pd diffraction peaks. When Sn was added to Pd/CNFs, the diffraction peaks moved to lower angles. HRTEM images revealed that the CNFs with cylindrical shape-like morphology and also Pd-Sn nanoparticles dispersed on carbon support. The catalytic activity and stability towards alcohol electro-oxidation in alkaline medium at room temperature was evaluated using cyclic voltammetry (CV), chronoamperometry (CA) and electrochemical impedance spectroscopy (EIS). The obtained Pd-Sn/CNFs electro-catalyst exhibited a better electro-catalytic activity than Pd/CNFs and Pd/C electro-catalysts for both methanol and ethanol oxidation. The improvement of the electrochemical performance was associated with the synergistic effect via the addition of Sn which modified the Pd atom arrangement, thereby promoting oxidation through a dehydrogenation pathway. Furthermore, SnO2 generates abundant OH species which helps with increasing the rate of the oxidative removal of carbon monoxide (CO) intermediates from Pd sites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.