We report the detailed temperature-dependent characteristics of Dy3+ doped SrAl2O4 phosphor. The phosphor synthesised using precipitation method was annealed at three different temperatures, specifically 800ºC, 900ºC, and 1000ºC. The three samples were analyzed using XRD, SEM, TEM, RAMAN, and FTIR. The observed photoluminescence emissions were consisting of peaks arising from the host SrAl2O4 as well as the dopant Dy3+. The crystallite sizes were found to be 27.22nm, 29.74nm, and 31.24nm, respectively, with the increase in annealing temperature. SEM, TEM images showed nearspherical, rod-like shapes of the crystals, and SAED confirmed the crystals were single-crystal. CIE analysis results showed that the colour coordinate was found to be very close to white colour in the three annealing temperatures, which is an advantage in the field of technology development.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.