When a discontinuity in material properties exists across a bonded interface, stresses are generated as a result of any thermal or mechanical loading. These stresses significantly affect strength and failure characteristics and may be large enough to prevent successful fabrication of a reliable joint. The use of an interlayer material to successfully reduce mismatch stresses, thereby preventing joint failure or improving joint strength and reliability, requires knowledge of failure mechanisms and of the effects of interlayer properties on the critical stress components.The origin of residual stresses developed during cooling of a ceramic-metal joint from an elevated fabrication temperature is illustrated qualitatively in Figure 1. Away from edges, the in-plane (parallel to interface) stresses are typically compressive in the ceramic and tensile in the metal. These stresses can cause cracking perpendicular to the interface, leading to spalling or delamination failures. Such failures are frequently observed in thin-film and coating geometries. Where the interface intersects a free edge, large shear and axial (perpendicular to the interface) stresses are generated. The edge stresses are typically tensile within the ceramic and tend to promote crack propagation within the ceramic parallel and adjacent to the interface. This is the most commonly observed failure mode in bonded structural components.
This paper aims to establish the mechanical, corrosion and failure analysis using online acoustic emission of Al7075 alloy, Al7075-B 4 C composite and Al7075-B 4 C-Al 2 O 3 hybrid composite with different Boron Carbide (B 4 C) content of 5, 10, 15 & 20% and Nano Aluminium Oxide (Al 2 O 3 ) content of 2% on a weight basis with the high energy stir casting method. The casted samples have been characterized by x-ray Diffraction (XRD), Thermo gravimetric analysis (TGA/DSC), Energy Dispersive Spectrum (EDS), and Scanning Electron Microscope (SEM). In case of hybrid composite, the hardness and the tensile strength decrease when the content of Al 2 O 3 increases. However, in the present research, the addition of B 4 C with nano Al 2 O 3 particles in certain proportions has increased the hardness and tensile strength. In addition, the tensile fractographs of the specimens were analysed using SEM. Acoustic Emission (AE) method was used for monitoring the acoustic energy that are released at the time of deformation process and early crack detection. The influence of the volume fraction of the B 4 C particulates on the microstructural and corrosion characteristics of Al7075-B 4 C with nano Al 2 O 3 metal matrix composites (MMCs) was also studied. It has been observed from the literature that the direct strengthening of composites occurs due to the presence of hard ceramic phase, while the indirect strengthening arises from the thermal mismatch between the matrix alloy and reinforcing phase during solidification. Based on the database for material properties, the application area of HAMCs has been proposed in the present review. The effects of nanomaterial dispersion in the metal matrix and the formation of interfacial precipitates on these properties are also addressed. Particular attention is paid to the fundamentals and the structure-property relationships of such novel Nano composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.