Distinct improvement in adhesion of diamond coatings on hard metal substrates was achieved by following substrate surface pretreatment [I]: First WC was removed from the substrate surface by etching with Murakami solution (K3[Fe(CN)6] in KOH), after which the Co binder network was etched with H2S04/H202 solution. Then diamond coatings were deposited on the substrates by hot-filament CVD. Apparently during the H2S04/H202 treatment of the Co binder a thin COO / CoS04 film forms, which prior to the diamond deposition would be reduced to CoS by the hydrogen and carbon species involved in the diamond synthesis. Since CoS is a stable compound at the diamond deposition temperatures, its Co vapor pressure and the Co surface mobility should be substantially lower than that for metallic Co. Thus the diamondhard metal interface is no longer influenced detrimentally by the metallic Co binder. This explanation has however not yet been confirmed by analytical methods such as SIMS and XPS. An alternative explanation would be the increassd roughness of the hard metal surface resulting from the removal of the Co binder and the formation of deep grooves on the interface which could lead to the improved adhesion. This however docs not explain why Co migration and other detrimental effects are not observed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.