In this work, properties of Nd3+ in Gd2O3-CaO-SiO2-B2O3 glass systems with composition 25Gd2O3-10CaO-10SiO2-(55-x)B2O3-xNd2O3 where x = 0.0, 0.5, 1.0, 1.5, 2.0 and 2.5 mol% were investigated. The optical absorption spectra show peaks at 4F3/2 (877 nm) , 4F5/2+2H9/2 (802 nm), 4F7/2+4S3/2 (743 nm), 4F9/2 (682 nm), 2H11/2 (627 nm), 2G7/2 +4G5/2 (582 nm), 4G7/2 +2K13/2 (527 nm), 4G11/2 (481 nm), 2P1/2 (427 nm) and 2L15/2 + 4D1/2 + 1I11/2+ 4D5/2+ 4D3/2 (355 nm) reflecting the Nd3+ ions in glass matrices. The densities were increased with increasing of Nd2O3 concentration. This indicates the increase of the molecular weight by the replacement of B2O3 with a heavier Nd2O3 oxide in the glass. The upconversion luminescence spectra show bands at 393 nm for all Nd2O3 concentration and the strongest intensity from 2.5 % mol of Nd2O3 was obtained. For NIR luminescence, the intensity of Nd3+ emission spectra increases with increasing concentrations of Nd3+ up to 1.5 mol% and beyond 1.5 mol% the concentration quenching is observed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.