This work deals with the preparation of cadmium sulfide (CdS) thin films by chemical bath deposition. The influence of the solution temperature is investigated in this study. We suggest that activation energy of the deposition rate measurement can be a tool for determining the nature of the deposition mechanism. We found that at low solution temperature, the growth mechanism proceeds via the ion by ion process, and found the corresponding activation energy equal to 0.06 eV. However, at higher solution temperature, the film deposition became via the cluster by cluster process, the growth rate activation energy is equal to 0.48 eV. The films' structural and optical properties were studied by x-ray diffraction analysis and UV–visible spectrophotometry. Structural analysis revealed that the deposited films have a cubic structure, and the crystallite size decreases with increasing deposition temperature. The transmission spectra of the film, in the visible range, show a high transmission coefficient (70%). The transmittance data analysis indicates that the optical band gap is closely related to the solution temperature. From this analysis, a direct band gap ranging from 2.21 to 2.34 eV was deduced. From the electrical characterization we inferred that CdS films are n-type and their dark conductivities reduced with increasing bath solution temperature. From the photoconductivity measurements we concluded that films deposited at low temperatures (less than 60 °C) or high temperatures (higher than 70 °C) have good optoelectronic properties suitable for utilization as a buffer layer in thin film solar cells.
Cadmium sulfide (CdS) thin films have been prepared by a simple technique such as chemical bath deposition (CBD). A set of samples CdS were deposited on glass substrates by varying the bath temperature from 55 to 75 °C at fixed deposition time (25 min) in order to investigate the effect of deposition temperature on CdS films physical properties. The determination of growth activation energy suggests that at low temperature CdS film growth is governed by the release of Cd2+ ions in the solution. The structural characterization indicated that the CdS films structure is cubic or hexagonal with preferential orientation along the direction (111) or (002), respectively. The optical characterization indicated that the films have a fairly high transparency, which varies between 55% and 80% in the visible range of the optical spectrum, the refractive index varies from 1.85 to 2.5 and the optical gap value of which can reach 2.2 eV. It can be suggested that these properties make these films perfectly suitable for their use as window film in thin films based solar cells.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.