The aim of this study was to fabricate a YAG/Al2O3 ceramic composite with different alumina nanoparticles using slip casting and the atmospheric sintering process. In addition, some mechanical properties such as hardness and elastic modules of this ceramic were evaluated using the nanoindention technique. The results showed that the rheological behavior of the slurry was optimized to the solid loading of 55 wt%; also, the relative density of the green body was enhanced up to 65%. Relative density was increased to 99.5% after sintering at 1700 °C for 12 h; further, the pore size (150 nm) was reduced to half of that of powder particles. It should be, however, noted that the optimum amount of alumina nanoparticles as a reinforcing agent in the matrix was less than 5%wt and the composite hardness was increased to 7.3%, as compared to the pure YAG ceramic.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.