The photoacoustic technique and the thermal relaxation method were used to determine the thermal conductivity of some representative samples obtained from an aluminumsilicon casting alloy A319. This material was solidified with an imposed unidirectional thermal gradient to obtain samples with different microstructures characterized by the secondary dendrite arm spacing, which increases as the solidification rate decreases. It was found that the thermal conductivity of the alloy decreases with an increase in the secondary dendrite arm spacing and a decrease in the integral dendrite perimeter.

Unidirectional solidification tests on an aluminum alloy were conducted with a computer-controlled instrumented rig. The alloys employed in this study were poured into isolated ingot molds (made of recrystallized alumina and covered with ceramic fiber) placed on top of a steel plate, coated either with a graphite-or ceramic-based paint in order to avoid sticking of the material. Thermal evolution during the test was captured by type-K thermocouples placed at different positions in both the ingot and the plate. The bottom surface of the plate was either cooled with water or left to cool in air. The heat-transfer coefficients across the aluminum-steel interface were evaluated by means of a finitedifference model. It was concluded that the heat-transfer rate depends on the conditions at the interface, such as the type of coating used to protect the plate, and the solidification reactions occurring on the aluminum during its solidification.

No abstract