Zirconium carbide–tungsten (ZrC–W) cermets were prepared by a novel in situ reaction sintering process. Compacted stoichiometric zirconium oxide (ZrO2) and tungsten carbide (WC) powders were heated to 2100°C, which produced cermets with 35 vol% ZrC and 65 vol% W consisting of an interpenetrating‐type microstructure with a relative density of ∼95%. The cermets had an elastic modulus of 274 GPa, a fracture toughness of 8.3 MPa·m1/2, and a flexural strength of 402 MPa. The ZrC content could be increased by adding excess ZrC or ZrO2 and carbon to the precursors, which increased the density to >98%. The solid‐state reaction between WC and ZrO2 and W–ZrC solid solution were also studied thermodynamically and experimentally.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.