Organic-inorganic hybrid materials synthesized by the sol-gel process have been developed for several years. This synthesis method can effectively overcome the defects of conventional composite materials. In this investigation, epoxy/SiO 2 hybrid material was synthesized by a sol-gel process with a precursor system. Tetraethoxysilane, water, and ethanol were mixed in appropriate proportions, varying the amounts of catalyst, alkalinity, and acidity, and then processed by a hydrolysis-condensation reaction at room temperature. The product synthesized with this process is called a precursor. The coupling agent ␥-glycidoxypropyl-methyldiethoxysilane (KBE-402) was used to modify the surface of the silica. The role of the coupling agent was to add covalent bonding between epoxy resin and silica, which reinforced the interfacial force of the hybrid material. The epoxy resin was mixed with precursor in different proportions and then cured at 170°C for 1 h. The thermal property of the epoxy/SiO 2 hybrid materials was studied by thermogravimetric analysis and DSC. From the results, we found the precursor prepared with acidity catalyst was better than that prepared with alkalinity catalyst. Coupling agent improved the thermal property of epoxy/ SiO 2 hybrid materials, especially when the temperature was high and the suitable amount of the coupling agent for the hybrid system was 5%. The glass-transition temperature of the hybrid materials was increased to adapt to the content of precursor from 80 to 113°C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.