Lead-free Sr(Hf0.5Zr0.5)O3-modified Bi0.5(Na0.8K0.2)0.5TiO3 (SHZ-BNKT) ceramics were synthesized using a conventional solid-state, mixed-oxide method. In complex solid solutions such as BNKT, the role of a ternary additive is important because it can break up the long-range dipole order, which destabilizes the ferroelectric phase leading to relaxor behavior. In this system, as verified by x-ray diffraction, SHZ was incorporated into the BNKT perovskite lattice throughout the studied compositional range. The coexistence of tetragonal and rhombohedral phase was observed for x = 0.00 and with the addition of SHZ, a transition to pseudocubic symmetry was observed, which is indicative of the onset of relaxor behavior. To characterize the relaxor properties of the material, the polarization–electric field hysteresis, dielectric, and electric-field-induced strain behaviors were studied as a function of composition. The temperature-dependent dielectric spectra showed frequency dependence for all the SHZ-modified BNKT ceramics, which is a typical characteristic of relaxor ferroelectrics. Furthermore, constriction in polarization loops and an absence of negative strain in the bipolar strain measurement for SHZ-modified BNKT compositions confirms that the addition of SHZ significantly disrupts the ferroelectric order. The addition of 2 mol. % SHZ in BNKT markedly enhanced the electric field-induced strain from 0.10% (for pure BNKT) to 0.33% (for 2% SHZ-BNKT). The corresponding normalized strain coefficient (d33∗=Smax/Emax) increased from 196 pm/V to 663 pm/V at a moderate electric field of 50 kV/cm. These results indicate that BNKT–SHZ ceramics can be designed for an improved strain response via a cation substitution-induced relaxor state for electromechanical actuator applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.