The growth rates of layer-by-layer (LbL) assemblies of polyelectrolytes (PEs) with oppositely charged polystyrene (PS) nanoparticles (NPs) as a function of molecular weight (MW) of the PEs, ionic strength of the media, and NP size and charge are systematically investigated. To optimize LbL growth, the effects of suspension concentration, pH of the media, and deposition time on the growth rate of multilayers are assessed. Both linear and exponential growth behaviors are observed and, under optimal conditions, films of up to around 1 μm thick can readily be assembled after 10 or so bilayers have been deposited. For many of the cases studied, an intermediate MW of PE leads to the fastest film buildup, for both cationic poly(ethyleneimine) deposited alternately with anionic PS NPs and for anionic poly(acrylic acid) deposited alternately with cationic PS NPs. The existence of an optimal MW suggests that growth rate is determined by a balance of thermodynamic factors, including density of polymer bridges between particles, and kinetic factors, specifically the diffusivity of polymer in the film. The optimal MW, however, is very sensitive to the materials used. Moreover, depending on the MW of the PE, increasing salinity could increase or decrease the growth kinetics. Finally, the surface morphology of the films is characterized with AFM and SEM to reveal that the roughness increases less than linearly with film thickness.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.