Since 2008, fine gauge (≤ 35 μm diameter) copper (Cu) wire has been rapidly replacing fine gauge gold (Au) wire in consumer, commercial, and industrial products [2–4]. The first wave of Cu wire products used bare, uncoated Cu wire which is soon to known having Cu-Al IMC corrosion induced by mobile chlorine ions in the epoxy mold compound system when IC parts are subjected to moisture related package stress tests such as biased HAST (Highly Accelerated Stress Test) [1–7]. Additionally, when comparing to Au wires, the 2nd bond process window of bare Cu wire can be very narrow and becomes a concern of moving into HVM (high volume manufacturing) [8]. Thus, palladium-coated Cu (PdCu) wire was introduced to the semiconductor assembly market aiming to provide more margin of passing biased HAST and enhance 2nd bond process capability [9–13]. However, the use of Pd-Cu wire is not a panacea to all Cu wire bond problems. One unique anomaly for Pd-Cu wire is the Cu ball void [1] which is observed only with Pd-Cu and not bare Cu ball bonds during HTSL (high temperature storage life) tests. The mechanism of forming Cu ball voids was proven to be the galvanized corrosion mechanism with Pd-Cu coupling. Significant factors affecting the formation rate of Cu ball voids are found to be baking temperature, EFO current settings, bonding parameters and mold compound additives (sulfur). Both anodic and cathodic chemical reactions will be proposed for Cu voids in this paper. Even though Cu void can be considered as a cosmetic defect for the majority of application since the peak temperature of device mission profile is always no larger than 175C. The application at extreme high temperature (for example, 190C) can actually cause electrical failure at the ball bon region due to the Cu void formation in terms of size and location at the Cu-Al IMC region. The main effect is due to the selected mold compound having high amount of metallic adhesion promoter which is sulfur-based and extensive high temperature storage test condition (190C). The FIB/SEM picture of failing ball bond due to Cu voids from this particular device will be presented in the paper. Thus, a newly developed doped Cu wire without Pd coating has been proposed by many wire suppliers to overcome Cu ball voids. However, doped Cu wires without Pd coating have suffered the same high volume manufacturing issues observed by bare Cu wires. For example, short tail and mean time between assist (MTBA) for doped Cu wires without Pd coating are both as poor as bare Cu wires. We will present high temperature storage test results obtained by doped PdCu wires in this paper. To balance high volume manufacturing issues and Cu void formation, doped PdCu wires are also proposed recently. Several doped PdCu wires whose extensive high temperature storage results (220C) will be presented in this paper. The worst case mold compound with high amount of sulfur based adhesion promoter has been used to test the effectiveness of these new wire types. At such harsh testing condition, there is one doped PdCu wire in our test can actually survive without electrical failed ball bond due to Cu voids. Factors of effectiveness of doped PdCu wires will be discussed in this paper. Authors have chosen to focus on Cu voids at both 1st bond (ball bond) and 2nd bond (wedge). 20 um wire diameter has been used for all test vehicle in this study. All controlling factors of eliminating Cu voids will surely be included at the end of this paper.
Wire bonding is still a very common method for connecting the pads on a chip to the package. During the ultrasonic wire bonding process, several failures such as ball neck failure, missing ball, bond metal peeling or crack etc., may be generated. Of those failures, bond pad peeling or crack is a phenomenon detected after bonding process and is identified as a critical reliability problem and is known as a complex defect to investigate. Bond pad cracks pose a high reliability risk and potential failure during environmental stress testing. Damage to the bond pad may be the result of sub optimized probe or wirebond process parameters, as well as poor pad design. In addition, bond pad cracks may be unintentionally induced by the cratering test chemical etch solution.There is a case where an assembly folk reported had a bond pad crack, but none of the parts have failure during electrical test or even after reliability stress. In such case, we believe the crack found at assembly was an artifact induced by etching chemical, resulting the over-rejecting the parts. This paper specifically discusses a comparative analysis of various bond pad etching methods and their impact on bond pad cracking.There are few interesting findings will also be shared during the discussions. Failure analysis results are also briefly discussed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.