Background: This study evaluated the prevalence of the signs and symptoms of temporomandibular joint disorder (TMD) among patients with TMD symptoms. Methods: Between September 2011 and December 2011, 243 consecutive patients (171 females, 72 males, mean age 41 years) who were referred to the Department of Prosthodontics, Faculty of Dentistry, Karadeniz Technical University, Trabzon were examined physically and completed a questionnaire regarding age, gender, social status, general health, antidepressant drug usage, dental status, limited mouth opening, temporomandibular joint (TMJ) sounds, and parafunctions (bruxism, clenching). The data were analyzed using the chi-square test and binary logistic regression model (alpha = 0.05). Results: With a frequency of 92%, pain in the temporal muscle was the most common symptom, followed by pain during mouth opening (89%) in both genders. TMJ pain at rest, pain in the masseter muscle, clicking, grinding, and anti-depressant use were significantly more frequent in females than males. Age (p=0.006; odds ratio 0.954; 95% CI 0.922-0.987) and missing teeth (p=0.003; odds ratio 3.753; 95% CI 1.589-8.863) had significant effects on the prevalence of TMD. Conclusion: Females had TMD signs and symptoms more frequently than males in the study population. The most common problem in both genders was pain.

No abstract

The autoclave polymerization technique exhibited significantly lower residual monomer content and greater hardness than conventional heat polymerization.

The aim of this study was to determine the effect of autoclave polymerization on the transverse strength of denture base polymers. To this end, 30 rectangular test specimens were fabricated of two heat-polymerized denture base polymers. The test groups were: (I) control, i.e., conventional water bath to polymerize resins by heat at 100°C for 30 minutes; (II) autoclave polymerization at 60°C for 30 minutes followed by 130°C for 10 minutes; and (III) autoclave polymerization at 60°C for 30 minutes followed by 130°C for 20 minutes. The specimens were tested with three-point bending test at a crosshead speed of 5 mm/min. It was revealed that the transverse strength of specimens increased with statistical significance when the autoclave was used for polymerization.