Pulsating tension tests with constant amplitude (CA) and variable amplitude (VA) were conducted to investigate the interior failure mechanisms of a carburized Cr steel, and a cumulative damage model with the fine granular area (FGA) formation process was proposed in this study. Such a steel represents the continuously descending S‐N (stress‐number of cycles) curve characteristics associated with inclusion‐FGA‐fisheye induced failure even under variable amplitude. Due to crack growth retardations and accelerations resulted from the interaction effect between stepwise resets of the applied stress, the crack morphology under variable amplitude loading is much rougher. The interior failure mechanism was elucidated in combination with the determination of stress intensity factor values at different crack tips. Based on proposed damage model, the agreement between the predicted and experimental results is fairly good within the factor‐of‐two range.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.