Bentonite clay nanoparticles without surface modification were used to prepare a polymer-based nanocomposite: Butyl acrylate (BA), methyl methacrylate (MMA), and acrylic acid (AA) were copolymerized as the matrix. The synthesis was carried out using seeded batch emulsion polymerization system. Bentonite was added up to 3 wt% and the metastable emulsions remained for a period over 6 months in storage at room temperature, to estimate the emulsion stability. Cast films were obtained from the aqueous dispersions and these were optically transparent. Scanning electron microscopy and X-ray scattering spectra showed that the copolymer chain had intercalated the Bentonite nanoplatelets, with aggregates into small crystalline clusters and dispersed through the polymer matrix. Differential scanning calorimetry showed that increasing the concentration of Bentonite increased the glass transition temperature, T g . Furthermore, uniaxial tensile deformation at room temperature showed that the elastic Youngs modulus, E, increased over an order of magnitude at 3 wt% Bentonite concentration. These results suggest that the molecular dynamics is inhibited, due to the associated restricted motions of the confined macromolecules within the gallery clay and the increment of the molecular weight. POLYM. COMPOS., 00:000-000, 2017. V C 2017 Society of Plastics Engineers FIG. 2. Solids analysis obtained as a function of polymerization time for (i) copolymer and the nanocomposites containing (a) 1 wt%, (b) 2 wt%, and (c) 3 wt% bentonite. Lines are only intended as guide to the eye. FIG. 3. Degree of conversion and coagulum amount of polymer/clay emulsions as a function of bentonite concentration. Lines are only intended as guide to the eye. FIG. 7. Photographs of copolymer/bentonite nanocomposites, about 1.0, 0.4, 0.2, and 0.5 mm in thickness, casted from their respective emulsions. The concentrations of bentonite are (a) 0 wt%, (b) 1 wt%, (c) 2 wt%, and (d) 3 wt%. FIG. 12. (a) TGA and (b) DTG curves for (i) copolymer and nanocomposites containing (ii) 1 wt%, (iii) 2 wt%, and (iv) 3 wt% of bentonite.
The incorporation of layered nano-silicates in polymer matrix greatly enhances the properties of the polymer. At present, there are many applications of polymer nanocomposites including coatings and architectural, they are also parts of automotive and construction industry among others. The acrylics employed at the present study were based on butyl acrylate (BA), styrene (STY), and methacrylic acid (MAA), and the nano-clay was Na-montomorillonite (MMT). The MMT clay was added to the polymer, which is the mixing matrix in a physical state solution called blend. Furthermore, their mechanical, thermal and wettability of especially prepared acrylic montmorillonite (MMT) nanocomposites were performed. By increasing the MMT in the polymer matrix concentration the Young’s modulus tends to increase it by an order of magnitude. However, by Differential Scanning Calorimetry (DSC), the thermograms show an increase in the glass transition temperature of nanocomposites for all weight percentages of MMT. Also, the wetting angle was determined, in order to know how much water is retained on the surface of the nanocomposite; the results showed that by increasing the particle of nano clay in the polymer matrix will induce a hydrophobic property to the nanocomposite.
Based on the nature of the links and interactions existing at the hybrid interface, hybrid materials can be broadly classified in two main designations: a) Hybrid compounds Class I, that include all systems with electrostatic forces, hydrogen bonding or Van der Waals interactions and b) Hybrid compounds Class II, showing that the inorganic and organic components are linked through strong covalent or ionic-covalent bonds. The physico–chemical properties of nanostructured copolymer acrylates based on butyl acrylate (BA), methyl methacrylate (MMA) and acrylic acid (AA) has been investigated employing un-modified SiO2 (Class I) and modified SiO2 particles (Class II) using 3-(trimethoxysilyl) propyl methacrylate (MPS) as compatibilizing agent. The synthesis was carried out using seeded batch emulsion polymerization system. Metastable nanostructured emulsions containing 1 wt% nanoparticles were obtained. Films casted from the in-situ nanostructured latex exhibited excellent optical transparency suggesting good nanoparticles dispersion. However, the mechanical properties showed by SiO2-MPS nanocomposite, are better than the Class I hybrid compounds. Therefore, SiO2-MPS surface treatment prior to polymerization enhances the physical properties of copolymer BA-MMA-AA film. The mass loss derivative traces for the polyacrylic nanocomposites and the neat polymer obtained by thermogravimetric analysis showed that the onset temperature for thermal decomposition was shifted towards a higher temperature than the neat polyacrylic, indicating the enhancement of thermal stability of the un-modified SiO2 nanocomposite. However, there is a decrease of 40°C in the decomposition temperature for the modified polyacrylic nanocomposite. The results obtained so far have shown that weak Van der Waals and H-bonding interactions may be sufficient to enable improvement of the physical properties of the acrylate nanocomposites.
The field of composites materials has evolved from the use of traditional fillers (e.g. carbon and glass fibers) to nanoscale fillers that add unique and often multifunctional properties to the neat polymer. Because nanoparticles have extremely high surface to volume ratios, that alter the mobility of polymer chains near their interfaces, even a small addition of nanoparticles. These components have the potential to drastically transform the properties of the host polymers. While the last decade has observed several advances in the field of nanocomposites, some recent reviews have made it clear that definitive structure-property relationships are insufficient in the literature. The influence of inorganic TiO2 nanoparticles on the dynamic mechanical properties and microstructure of copolymer based on Butyl acrylate - Methyl methacrylate - Acrylic Acid has been investigated. The mechanical relaxations of the reinforced copolymer/TiO2 composites were studied under tension mode. Addition of TiO2 nanoparticles to acrylic copolymer produced a decrease in the glass transition temperature. Dynamic mechanical analysis (DMA) showed that the local motions associated with the alpha-transition (40°C) are enhanced as the frequency of oscillation increases, i.e. the tan d maximum increases at higher frequencies. The addition of TiO2 nanoparticles reduces significantly the strength of the alpha-transition. Thus, the cooperative molecular motions involving segments of the molecular chains associated with the alpha-transition were compromised by the presence of TiO2 nanoparticles resulting in a decrement of the storage modulus.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.