Aim: To determine differences in marginal adaptation between a conventional composite resin and a monoincremental resin with sonic activation. Materials and methods: 32 composite resin discs of 2.5mm in diameter and 2mm thick were fabricated in a propylene matrix and distributed in 2 groups of 16 samples each. Groups 1 Filtek TM Z350XT resin; Group 2 SonicFill TM resin with sonic activation. The gap generated between the resin and the matrix as a result of the polymerization shrinkage was analyzed in microns using a microscope at a magnification of 40X. The percentage of the lineal polymerization shrinkage was also calculated. To calculate differences in marginal adaptation between the two resins statistical analysis was performed using the unpaired t-test. Results: The extent of the gaps measured in microns and their respective standard deviations were SonicFill TM 9.95±3.05and Filtek TM Z350XT 10.21±5.14 (p=.86). Conclusion: The use of the monoincremental resin system with sonic activation shows a marginal adaptation similar to that of conventional resin composites, with no statistically significant differences between the studied resins.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.