The effect of cathodic activation of sprayed La 0.8 Sr 0.2 MnO 3 (LSM) films has been studied by electrochemical spectroscopy impedance (EIS). LSM powder was prepared by a citrate route and X-ray diffraction analyses show a complete LSM crystallization without La 2 O 3 or La (OH) 3 as side products. Porosity and grain size estimated from scanning electronic microscopy gave values of 33% and 100 nm, respectively. EIS measurement was performed on a Pt/yttria-stabilized zirconia/LSM cell before and after a cathodic current load (300 mA/cm 2 ) on LSM electrode. The relaxation process, which is time-dependent, has been investigated. A drastic decrease of the electrode resistance was noticed just after applying the cathodic current, but after 9 h at optimized valence configuration in air at 850°C, the recorded polarization resistance gradually enhanced until it almost reached the initial value. The resulting diagrams have been fitted using a Gerischer associated with a resistor and constant phase elements. This simple method has permitted us to observe that only the electrode interfaces are modified by a cathodic activation and the microstructure remains nearly constant.
RESUMOO grande desafio para se melhorar o desenvolvimento de pilhas a combustível de óxido sólido (PACOS) é diminuir as resistências de polarização ôhmica e de polarização de concentração, sobretudo no catodo. Uma alternativa efetiva é a introdução de uma camada catódica funcional entre o eletrólito e o catodo convencional. Esta camada funcional é um compósito constituído pelos materiais de eletrólito e catodo que neste caso são a zircônia estabilizada com ítria (ZEI) e a manganita de lantânio e estrôncio (MSL). Esta camada melhora o contato entre o catodo e o eletrólito diminuindo a resistência ôhmica de polarização de concentração devido ao aumento do número de pontos de contato triplo (PCT) no volume do material.Neste trabalho, duas meias células foram preparadas: a primeira é constituída por um filme catódico funcional (50% p/p) e a camada coletora de corrente depositados sobre uma pastilha de ZEI. A segunda meia célula é composta apenas pela camada catódica de MSL também depositada sobre a pastilha de ZEI.O estudo elétrico foi realizado por espectroscopia de impedância na faixa de temperatura entre 700 e 900 °C. As resistências das amostras diminuíram com o aumento da temperatura e, foi observado que a meia célula que possuía o catodo funcional apresentou menores resistências elétricas. Após tratamento térmico a 750°C por 3 dias foi verificado que a amostra sem a camada funcional apresentou um semicírculo adicional no diagrama de impedância caracterizado como uma resistência devida a baixa aderência eletrólito/catodo. Este fenômeno foi confirmado por imagens de microscopia eletrônica de varredura (MEV). Palavras-chaves: MLS, Espectroscopia de impedância, catodo funcional. The importance of the functional layer in SOFC half cathodic cell ABSTRACTThe greatest challenge to improve SOCF (Solid Oxide Fuel Cell) development is to decrease polarization and ohmic concentration resistances mainly for the cathode. One effective alternative is the introduction of a functional cathode layer between the electrolyte and the conventional cathode. This functional cathode layer is a composite constituted by the electrolyte and cathode materials, in this case, yttria stabilized zirconia (YSZ) and lanthanum doped strontium (LSM). This layer improves the contact between the cathode and the electrolyte decreasing the ohmic concentration polarization due to the increasing of triple contact points (TPB) in the bulk concentration.In this work, two half cells were prepared: the first one is constituted by a functional cathode film (50% in weight), and a collecting current layer (LSM) both deposited on a YSZ pellet. The second half cell is composed by a LSM cathode layer deposited on the YSZ Tosoh pellet.The electric study has been realized by Impedance Spectroscopy varying the temperature from 700 to 900 ºC. The two half cells resistance decreased with increasing the temperature, and it has noted that the half cell with the functional cathode layer presented the lowest resistance. After annealing at 750 °C for 3 days, the sample wi...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.