Interactions between ceria (CeO2) and supported metals greatly enhance rates for a number of important reactions. However, direct relationships between structure and function in these catalysts have been difficult to extract because the samples studied either were heterogeneous or were model systems dissimilar to working catalysts. We report rate measurements on samples in which the length of the ceria-metal interface was tailored by the use of monodisperse nickel, palladium, and platinum nanocrystals. We found that carbon monoxide oxidation in ceria-based catalysts is greatly enhanced at the ceria-metal interface sites for a range of group VIII metal catalysts, clarifying the pivotal role played by the support.

Well-controlled synthesis of nanocrystals is necessary to unambiguously correlate the structural properties of nanocrystals with the catalytic properties. The most common low-index surfaces are (111) and (100). Therefore, model materials with {111} and {100} facets are highly desirable, in order to understand the catalytic properties of (111) and (100) surfaces for various structure-sensitive reactions. We report a solution-phase synthesis using metal carbonyls as additives. This synthetic method produces highly monodisperse Pt octahedra and icosahedra as the model of Pt{111}, Pt cubes as the model of Pt{100}, respectively. Several other morphologies, such as truncated cubes, cuboctahedra, spheres, tetrapods, star-shaped octapods, multipods, and hyper-branched structure, are produced, as well. A bifunctional role of metal carbonyl in the synthesis is identified: zerovalent transition metal decomposed from metal carbonyl acts as a shape-directing agent, while CO provides the reducing power. These high-quality shape-controlled Pt nanocrystals are suitable for model catalyst studies.

2 nm PdIn intermetallic alloy (cubic, CsCl type) nanoparticle catalyst was near 100% selective to ethane dehydrogenation at 600 °C (at 15% conversion) with a dehydrogenation TOR almost 10 times higher than that of monometallic Pd.

Large-area icosahedral-AB(13)-type Pt-Pd binary superlattices (BNSLs) are fabricated through self-assembly of 6 nm Pd nanocrystals (NCs) and 13 nm Pt octahedra at a liquid-air interface. The Pt-Pd BNSLs enable a high activity toward electrocatalysis of oxygen reduction reaction (ORR) by successfully exploiting the shape effects of Pt NCs and synergistic effects of Pt-Pd into a single crystalline nanostructure. The Pt-Pd BNSLs are promising catalysts for the oxygen electrode of fuel cells.