The syntheses and single‐crystal X‐ray structures of a series of Mo–imido alkylidene N‐heterocyclic carbene (NHC) complexes (1–15) and of the first complexes containing bidentate NHC‐phenolate ligands (16–18) are reported. Mo(N‐2,6‐Me2‐C6H3)((1‐R‐phenethyl)‐3‐mesitylimidazolidin‐2‐ylidene)(CHR)(OTf)2 (R=CMe2Ph, 1) is the first enantiomerically pure Mo–imido alkylidene NHC catalyst. With [Mo(N‐2,6‐Me2‐C6H3)(IMes)(CHR)(CH3CN)(OTf)(CH3CN)+ B(ArF)4−] (7), turnover numbers up to 545 000 were achieved in the homometathesis (HM) of 1‐octene and 1‐nonene (≤95 % E). With 7 and 1‐nonene, a turnover frequency (TOF4 min) of 8860 min−1 was determined. Productivity and E/Z‐selectivity were correlated with catalyst structure. For 1, Mo(N‐3,5‐Me2‐C6H3)(IMesH2)(CHR)(OTf)2 (9) and Mo(N‐3,5‐Me2‐C6H3)(IMes)(CHR)(OTf)2 (10), productivity was correlated with the coalescence temperature of the two triflates, determined by variable‐temperature 19F NMR spectroscopy. The square‐planar conformer is postulated to be the most relevant for the catalyst activation.

The synthesis and single-crystal X-ray structures of the novel molybdenum imido alkylidene N-heterocyclic carbene complexes [Mo(N-2,6-Me2C6H3)(IMesH2)(CHCMe2Ph)(OTf)2] (3), [Mo(N-2,6-Me2C6H3)(IMes)(CHCMe2Ph)(OTf)2] (4), [Mo(N-2,6-Me2C6H3)(IMesH2)(CHCMe2Ph)(OTf){OCH(CF3)2}] (5), [Mo(N-2,6-Me2C6H3)(CH3CN)(IMesH2)(CHCMe2Ph)(OTf)](+)BArF(-) (6), [Mo(N-2,6-Cl2C6H3)(IMesH2)(CHCMe3)(OTf)2] (7) and [Mo(N-2,6-Cl2C6H3)(IMes)(CHCMe3)(OTf)2] (8) are reported (IMesH2=1,3-dimesitylimidazolidin-2-ylidene, IMes=1,3-dimesitylimidazolin-2-ylidene, BArF(-)=tetrakis-[3,5-bis(trifluoromethyl)phenyl] borate, OTf=CF3SO3(-)). Also, silica-immobilized versions I1 and I2 were prepared. Catalysts 3-8, I1 and I2 were used in homo-, cross-, and ring-closing metathesis (RCM) reactions and in the cyclopolymerization of α,ω-diynes. In the RCM of α,ω-dienes, in the homometathesis of 1-alkenes, and in the ethenolysis of cyclooctene, turnover numbers (TONs) up to 100,000, 210,000 and 30,000, respectively, were achieved. With I1 and I2, virtually Mo-free products were obtained (<3 ppm Mo). With 1,6-hepta- and 1,7-octadiynes, catalysts 3, 4, and 5 allowed for the regioselective cyclopolymerization of 4,4-bis(ethoxycarbonyl)-1,6-heptadiyne, 4,4-bis(hydroxymethyl)-1,6-heptadiyne, 4,4-bis[(3,5-diethoxybenzoyloxy)methyl]-1,6-heptadiyne, 4,4,5,5-tetrakis(ethoxycarbonyl)-1,7-octadiyne, and 1,6-heptadiyne-4-carboxylic acid, underlining the high functional-group tolerance of these novel Group 6 metal alkylidenes.

No abstract

Designing supported alkene metathesis catalysts with high activity and stability is still a challenge, despite significant advances in the last years. Described herein is the combination of strong σ-donating N-heterocyclic carbene ligands with weak σ-donating surface silanolates and cationic tungsten sites leading to highly active and stable alkene metathesis catalysts. These well-defined silica-supported catalysts, [(≡SiO)W(=O)(=CHCMe2 Ph)(IMes)(OTf)] and [(≡SiO)W(=O)(=CHCMe2 Ph)(IMes)(+) ][B(Ar(F) )4 (-) ] [IMes=1,3-bis(2,4,6-trimethylphenyl)-imidazol-2-ylidene, B(Ar(F) )4 =B(3,5-(CF3 )2 C6 H3 )4 ] catalyze alkene metathesis, and the cationic species display unprecedented activity for a broad range of substrates, especially for terminal olefins with turnover numbers above 1.2 million for propene.

The pentacoordinated, 16-valence electron (VE) Mo imido alkylidene N-heterocyclic carbene (NHC) complexes I1-I5 and the hexacoordinated 18-VE Mo imido alkylidene NHC complexes 1-4, 8, 10 and 12 containing a chelating ligand have been prepared and used as thermally latent catalysts in the ring-opening metathesis polymerization (ROMP) of dicyclopentadiene (DCPD). Both 10 and 12 are the first Mo imido alkylidene complexes with a chelating alkylidene featuring a carboxylate group. Complexes I1-I3 and I5 as well as 1-4 proved to be fully thermally latent in the presence of DCPD. With the changes in both the electronic and steric situation at the imido ligand provided by these pre-catalysts, different temperatures of the onset of polymerization (T =65-140 °C) and for the exothermic maximum of the curing curve (T =98-183 °C) of DCPD were achieved. Also, the degree of crosslinking was successfully varied as indicated by swelling experiments in toluene, which revealed degrees of swelling between 0 and 50 %. While the introduction of a chelating alkylidene increases T , the introduction of more electron-donating anionic ligands (tert-butoxide, phenoxide) resulted in a drastic reduction in T , underlining the high flexibility of these systems. The hexacoordinated high-oxidation state molybdenum imido alkylidene NHC complexes 2, 3 and 4 were stable under air for at least twelve hours in the solid state.