Aluminium with silicon as alloying element, form a class of material providing the most significant part of all material casting manufactured materials. These alloys have a wide range of applications in the automotive and aerospace industries. It is widely recognized that moderate addition of silicon to aluminum, significantly improves the resulting mechanical properties. Hypoeutectic Al-Si alloys were used in the present experimental study to investigate the solidification parameters effect and Si 3-5 wt% addition on the microstructural features and resulting hardness in a vertical directional solidification system. The hypoeutectic alloys were directionally solidified under transient heat flow conditions in a range of cooling rates from 0.3 to 4 ºC/s. Characterization analyses by optical microscopy indicate clearly that secondary dendritic arm spacing (λ 2 ) increases significantly with the decrease in solidification speed (S P ) and cooling rate (Ṫ). On the other hand, experimental growth laws relating the secondary dendritic arm spacing (λ 2 ) to the solidification speed (S P ) and cooling rate (Ṫ) indicate that Si addition from 3 wt% to 5 wt% has induced a thickening effect leading to increase in λ 2 . While, experimental results have shown that the resulting hardness increase as solidification processing parameters (S P and Ṫ ) increase. Results of Vickers hardness test for Al-5 wt% Si alloy has hardness increase of 18 % from that of Al-3 wt% Si alloy with mean values of 26 and 22 HV, respectively.
The microstructure and mechanical properties of cast materials are strongly dependent on the thermal history during solidification process. The global casting industry has faced major challenges, i.e., customers increasingly demand completely finished cast parts as well as complexity of casting alloys are rising. Therefore, the previous knowledge the solidification conditions effects on the ascast ingot microstructure and mechanical properties resulting is very useful in the casting industry in order to improve the casting quality. In this present paper, the thermal parameters effects on the microstructure, microhardness and microsegregation of a Cu-20 wt.% Sn alloy under transient heat flow conditions were experimentally investigated. The experimental observations indicate that the tertiary dendritic arm spacing (λ 3), microsegregation and microhardness are affected by the thermal parameters (solidification speed and cooling rate). Solidification speed (S S) associated with increasing cooling rate (R C) are found to contribute to the decreasing tertiary dendritic arm spacing (λ 3). However, cooling rates from 11.36 °C/s to 0.65 °C/s were not found to affect significantly the microhardness along the ingot length. The solute concentration (Sn) in solid region were calculated by Scheil and Clyne-Kurz equation, and used in the predictions of microsegregation profiles. The results calculated by equations, have shown deviations from the experimental data. It is well known that it is very difficult to calculate these concentration profiles using the equilibrium partition coefficient, since frequently castings solidify under non-equilibrium conditions and the solidification process is known as non-equilibrium solidification. For this reason, effect of solidification speed (S S) was considered into equations through effective partition coefficient (k ef) that has been determined for the range of solidification speed experimentally examined between 0.19 and 0.89 mm/s. However, results calculated by Scheil and Clyne-Kurz equation using the effective partition coefficient (k ef), yielded discrepancies from the experimental results. Because of its deviations between calculated and experimental data, an experimental equation with effective partition coefficient (k ef), is considered in present work, showing an excellent agreement with the experimental data.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.