In this paper, we report the overall design, fabrication and optical characterization of single and multiple resonant micro-structures patterned on the UV210 polymer and shaped by adequate deep-UV lithography procedures. Various families of ring and racetrack forms are investigated with different geometrical dimensions linked to the micro-resonators and the specific taper-waveguides and gaps allowing the optimized coupling. Well defined photonic structures families in the sub-micrometer range obtained by this deep UV-light process are clearly confirmed through scanning electron microscopy. In order to evaluate and quantify the efficiency of the submicrometer coupling, the recirculation of the light and the quality of the optical resonance aspects, a global study including top view intensity imaging, spectral measurements and Fast Fourier Transform analysis is performed for all these devices based on single and multiple family resonators. The experimental TE-mode resonance transmissions reveal a complete agreement with the period of the theoretically expected resonances. A maximum value of the quality factor Q = 3.5 x 10 3 at 1035 nm with a 3.2 times higher resonance contrast is assessed for cascade of triple micro-resonators respect to the photonic devices based on only one micro-resonator. In addition, these UV210 circuits made of specific tapers coupling to cascade loops act directly on the improvement of the evanescent coupling and resonances in terms of quality factor and extinction rate, by selecting successively and more precisely the optical mode resonance. All these designs and low cost technological reproducible steps, and furthermore the devices and protocol measurements are markedly suitable for mass fabrication and metrology applications.
Spherical silver nanoparticles (diameter 3 nm) were transformed by means of photochemical synthesis using superluminescent LEDs. Flat rounded (21 nm) and decahedral nanoparticles (78 nm) were, respectively, obtained when the colloid was exposed to green and blue radiation. Furthermore, by changing from blue to green radiation at different exposure times, various morphologies and sizes were obtained. Exposure times shorter than 30 min of blue radiation followed by green radiation resulted on different morphologies such as twine rounded (42 nm), flat elongated (peanuts, 17 nm), and flat rounded nanoparticles (11 and 24 nm). Times longer than 45 min produced decahedral nanoparticles with corners ranging from rounded to sharp (size 71-78 nm). Additionally, these results showed that by controlling morphologies and sizes through the combination of blue and green light at different exposure times, it was possible to tune the plasmon band from 511 to 594 nm. Moreover, controlling the morphology of nanoparticles is of prime importance in order to exploit their properties as part of novel emerging technologies.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.