The influence of dysprosia addition on the sintering and resulting microstructure of nano‐grained CeO2 ceramics was investigated as functions of the spark plasma sintering parameters. The addition of Dy2O3 (forming a solid solution) resulted in an increase in relative density and a decrease in grain size in sintered samples. The relative density of samples with Dy2O3 content of 6 and 10 mol% was over 95% when sintered at 1050°C under 500 MPa for holding times as short as 5 min. The application of high pressure facilitated the consolidation to relatively high densities with minimal grain growth. Heating rate and holding time, however, had insignificant effect on density but a measurable effect on grain size.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.