Cesium lead halide pervoskite semiconductors are being extensively studied due to unprecedentedly high luminescence efficiency and concomitant narrow emission line width. Here, we report photophysical properties of CsPbBr 3 quantum dots having different sizes. Notably 5.5 nm sized CsPbBr 3 quantum dots reveal 95% photoluminescence (PL) quantum yield at room temperature. Moreover, signature of the stimulated emission is observed at low temperature for excitation fluence as low as ∼4.16 μW (Xe lamp excitation). Even though CsPbBr 3 quantum dots reveal the red shift in band gap at low temperature, similar to the single crystal, the exciton−phonon interaction is profoundly affected by the quantum size effects. Temperature-dependent optical studies reveal an anomalous decrease in exciton-LO phonon coupling in small-sized quantum dots aside from expected higher exciton binding energy. Observed stimulated emission in low-sized CsPbBr 3 quantum dots has implications in realizing a quantum dot based laser.
CsPbCl3 nanocrystals (NCs) are known to show low photoluminescence
(PL) quantum efficiency compared to CsPbBr3 NCs. In the
present work, at 20 K, stimulated emission is observed from CsPbCl3 NCs at low excitation intensity. Efforts are made to understand
the optical behavior and structural properties of chemically grown,
5.3 ± 1.1 nm sized CsPbCl3 NCs. Bulk CsPbCl3 is known to become cubic at 320 K, while, NCs are cubic or tetragonal
at room temperature. Temperature dependent PL studies on CsPbCl3 NCs are carried out in a wide temperature range. The primary
experimental finding is, about 90 times rise in PL emission intensity
and existence of multiple sharp features at low temperature attributable
to free exciton, bound excitons, phonon replica along with the defect
related emission and stimulated emission. The optical phonon energy
is about 26 meV with coupling constant of 54 meV in ∼5.3 nm
sized CsPbCl3 NCs. Structural phase transition in CsPbCl3 NCs at about 200 K is also observed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.