Monolithic zirconia use is partially restricted due to the zirconia low translucency. The new "augmented translucency" zirconia showed a modest but perceptible increase in translucency and a similar flexural resistance, thus increasing the clinically suitable thickness range with optimized aesthetic and resistance. (J Esthet RestorDent 28:S32-S39, 2016).
The zirconia composition heavily influenced both the flexural strength and the translucency. Different percentages of Yittria and Alumina result in new materials with intermediate properties in between the conventional zirconia and lithium disilicate. Clinical indications for Zirconia Aadva NT should be limited up to three-unit span bridges.
Manual finishing/polishing for 60 seconds and glazing paste are the most effective procedures in lowering the roughness of CAD/CAM silica-based glass ceramics. Manual finishing/polishing for 60 seconds allows milled silica-based glass ceramics to yield a higher gloss. VITA Suprinity displayed higher polishability than IPS e.max CAD.
This study aimed at evaluating the effects of different surface conditionings on the microshear bond strength (µSBS) of a self-adhesive resin cement to VITA Suprinity (ZLS) and IPS e.max CAD (LD). Three surface conditioning protocols were performed on ZLS and LD before luting with a self-adhesive resin cement (RelyX Unicem 2, RXU): hydrofluoric acid (HF), HF + silane (HF + S), or Monobond Etch & Prime (EP). In each group, 15 cylindrical buildups of RXU were prepared on five milled bars and submitted to a µSBS test. Data were statistically analyzed with two-way ANOVA and Tukey’s post hoc test (p < 0.05). Failure modes were recorded and classified as adhesive, mixed, cohesive in resin, or ceramic, and statistically analyzed with Fisher’s exact test (p = 0.05). One additional bar per group was used for the morphological characterization of the conditioned surface by means of SEM. The material per se did not significantly influence adhesion (p = 0.744). Conditioning protocol was a significant factor: EP yielded significantly higher μSBS than HF (p = 0.005), while no significant differences emerged between EP and HF + S (p = 0.107), or HF + S and HF (p = 0.387). The material-conditioning protocol interaction was not statistically significant (p = 0.109). Significant intergroup differences were found in distribution of failure modes: mixed failures were predominant in the ZLS/EP group, while the other groups showed a prevalence of adhesive failures. The self-etching primer showed promising results in terms of immediate bond strength of a self-adhesive resin cement to lithium-silica-based glass ceramics, suggesting its alternative use to hydrofluoric acid and silane conditioning protocols.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.