The machining process is still a very relevant process in today’s industry, being used to produce high quality parts for multiple industry sectors. The machining processes are heavily researched, with the focus on the improvement of these processes. One of these process improvements was the creation and implementation of tool coatings in various machining operations. These coatings improved overall process productivity and tool-life, with new coatings being developed for various machining applications. TiAlN coatings are still very present in today’s industry, being used due to its incredible wear behavior at high machining speeds, high mechanical properties, having a high-thermal stability and high corrosion resistance even at high machining temperatures. Novel TiAlN-based coatings doped with Ru, Mo and Ta are currently under investigation, as they show tremendous potential in terms of mechanical properties and wear behavior improvement. With the improvement of deposition technology, recent research seems to focus primarily on the study of nanolayered and nanocomposite TiAlN-based coatings, as the thinner layers improve drastically these coating’s beneficial properties for machining applications. In this review, the recent developments of TiAlN-based coatings are going to be presented, analyzed and their mechanical properties and cutting behavior for the turning and milling processes are compared.
Abstract:It is well known that injection of glass fibre-reinforced plastics (GFRP) causes abrasive wear in moulds' cavities and runners. Physical vapour deposition (PVD) coatings are intensively used to improve the wear resistance of different tools, also being one of the most promising ways to increase the moulds' lifespan, mainly when used with plastics strongly reinforced with glass fibres. This work compares four different thin, hard coatings obtained using the PVD magnetron sputtering process: TiAlN, TiAlSiN, CrN/TiAlCrSiN and CrN/CrCN/DLC. The first two are monolayer coatings while the last ones are nanostructured and consist of multilayer systems. In order to carry out the corresponding tribological characterization, two different approaches were selected: A laboratorial method, using micro-abrasion wear tests based on a ball-cratering configuration, and an industrial mode, analysing the wear resistance of the coated samples when inserted in a plastic injection mould. As expected, the wear phenomena are not equivalent and the results between micro-abrasion and industrial tests are not similar due to the different means used to promote the abrasion. The best wear resistance performance in the laboratorial wear tests was attained by the TiAlN monolayer coating while the best performance in the industrial wear tests was obtained by the CrN/TiAlCrSiN nanostructured multilayer coating.
a b s t r a c tAbrasion by glass fibers during injection molding of fiber reinforced plastics raises new challenges to the wear performance of the molds. In the last few decades, a large number of PVD and CVD coatings have been developed with the aim of minimizing abrasion problems. In this work, two different coatings were tested in order to increase the wear resistance of the surface of a mold used for glass fiber reinforced plastics: TiAlSiN and CrN/CrCN/DLC. TiAlSiN was deposited as a graded monolayer coating while CrN/CrCN/DLC was a nanostructured coating consisting of three distinct layers. Both coatings were produced by PVD unbalanced magnetron sputtering and were characterized using scanning electron microscopy (SEM) provided with energy dispersive spectroscopy (EDS), atomic force microscopy (AFM), micro hardness (MH) and scratch test analysis. Coating morphology, thickness, roughness, chemical composition and structure, hardness and adhesion to the substrate were investigated. Wear resistance was characterized through industrial tests with coated samples and an uncoated reference sample inserted in a feed channel of a plastic injection mold working with 30 wt.% glass fiber reinforced polypropylene. Results after 45,000 injection cycles indicate that the wear resistance of the mold was increased by a factor of 25 and 58, by the TiAlSiN and CrN/CrCN/DLC coatings, respectively, over the uncoated mold steel.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.