The spatial structure of the J-aggregates of meso-tetra(4-sulfonatophenyl)porphine (TPPS4) formed in acidic aqueous solutions and coated on silicon substrates was analyzed by means of atomic force microscopy (AFM). The AFM experiments indicate the presence of the stripelike J-aggregate structures on the surface. The size of the individual stripes ranged from 4.5 × 40 × 200 to 4.5 × 40 × 1000 nm3 (height × width × length). The length of the stripelike structures varied, whereas stripe width and thickness remained unchanged. The stripes stacked into larger domains, “fibers”, containing typically 2−20 stripes aligned parallel with a longitudinal shift with respect to each other. The size of individual stripes remained the same when interacting side-by-side in fibers. At lower magnification it is clearly seen that fibers form a network-like structure. The J-aggregates assemble into large (up to several millimeters) bushlike structures. It takes several weeks to form such structures in acidic aqueous solutions. On the basis of our experimental findings, it is also suggested that the stripes consist of rings that form nanotube-like TPPS4 J-aggregates, which are flattened as a result of attractive interactions with the substrate.

Theranostic nanoagents targeted for personalized medicine provide a unified platform for therapeutics and diagnostics. To be able to discretely control each individually, allows for safer, more precise, and truly multifunctional theranostics. Rare earth doped nanoparticles can be rationally tailored to best match this condition with the aid of core/shell engineering. In such nanoparticles, the light‐mediated theranostic approach is functionally decoupled—therapeutics or diagnostics are prompted on‐demand, by wavelength‐specific excitation. These decoupled rare earth nanoparticles (dNPs) operate entirely under near‐infrared (NIR) excitation, for minimized light interference with the target and extended tissue depth action. Under heating‐free 806 nm irradiation, dNPs behave solely as high‐contrast NIR‐to‐NIR optical markers and nanothermometers, visualizing and probing the area of interest without prompting the therapeutic effect beforehand. On the contrary, 980 nm NIR irradiation is upconverted by the dNPs to UV/visible light, which triggers secondary photochemical processes, e.g., generation of reactive oxygen species by photosensitizers coupled to the dNPs, causing damage to cancer cells. Additionally, integration of NIR nanothermometry helps to control the temperature in the vicinity of the dNPs avoiding possible overheating and quenching of upconversion (UC) emission, harnessed for photodynamic therapy. Overall, a new direction is outlined in the development of state‐of‐the‐art rare earth based theranostic nanoplatforms.

Background:The purpose of this study was to elucidate the mechanism of natural uptake of nonfunctionalized quantum dots in comparison with microinjected quantum dots by focusing on their time-dependent accumulation and intracellular localization in different cell lines. Methods:The accumulation dynamics of nontargeted CdSe/ZnS carboxyl-coated quantum dots (emission peak 625 nm) was analyzed in NIH3T3, MCF-7, and HepG2 cells by applying the methods of confocal and steady-state fluorescence spectroscopy. Intracellular colocalization of the quantum dots was investigated by staining with Lysotracker ® . Results:The uptake of quantum dots into cells was dramatically reduced at a low temperature (4°C), indicating that the process is energy-dependent. The uptake kinetics and imaging of intracellular localization of quantum dots revealed three accumulation stages of carboxyl-coated quantum dots at 37°C, ie, a plateau stage, growth stage, and a saturation stage, which comprised four morphological phases: adherence to the cell membrane; formation of granulated clusters spread throughout the cytoplasm; localization of granulated clusters in the perinuclear region; and formation of multivesicular body-like structures and their redistribution in the cytoplasm. Diverse quantum dots containing intracellular vesicles in the range of approximately 0.5-8 µm in diameter were observed in the cytoplasm, but none were found in the nucleus. Vesicles containing quantum dots formed multivesicular body-like structures in NIH3T3 cells after 24 hours of incubation, which were Lysotracker-negative in serum-free medium and Lysotracker-positive in complete medium. The microinjected quantum dots remained uniformly distributed in the cytosol for at least 24 hours. Conclusion: Natural uptake of quantum dots in cells occurs through three accumulation stages via a mechanism requiring energy. The sharp contrast of the intracellular distribution after microinjection of quantum dots in comparison with incubation as well as the limited transfer of quantum dots from vesicles into the cytosol and vice versa support the endocytotic origin of the natural uptake of quantum dots. Quantum dots with proteins adsorbed from the culture medium had a different fate in the final stage of accumulation from that of the protein-free quantum dots, implying different internalization pathways.

No abstract

Semiconductor nanoparticles (quantum dots) are promising fluorescent markers, but it is very little known about interaction of quantum dots with biological molecules. In this study, interaction of CdTe quantum dots coated with thioglycolic acid (TGA) with bovine serum albumin was investigated. Steady state spectroscopy, atomic force microscopy, electron microscopy and dynamic light scattering methods were used. It was explored how bovine serum albumin affects stability and spectral properties of quantum dots in aqueous media. CdTe–TGA quantum dots in aqueous solution appeared to be not stable and precipitated. Interaction with bovine serum albumin significantly enhanced stability and photoluminescence quantum yield of quantum dots and prevented quantum dots from aggregating.

No abstract

The uptake and distribution of negatively charged superparamagnetic iron oxide (Fe3O4) nanoparticles (SPIONs) in mouse embryonic fibroblasts NIH3T3, and magnetic resonance imaging (MRI) signal influenced by SPIONs injected into experimental animals, were visualized and investigated. Cellular uptake and distribution of the SPIONs in NIH3T3 after staining with Prussian Blue were investigated by a bright-field microscope equipped with digital color camera. SPIONs were localized in vesicles, mostly placed near the nucleus. Toxicity of SPION nanoparticles tested with cell viability assay (XTT) was estimated. The viability of NIH3T3 cells remains approximately 95% within 3–24 h of incubation, and only a slight decrease of viability was observed after 48 h of incubation. MRI studies on Wistar rats using a clinical 1.5 T MRI scanner were showing that SPIONs give a negative contrast in the MRI. The dynamic MRI measurements of the SPION clearance from the injection site shows that SPIONs slowly disappear from injection sites and only a low concentration of nanoparticles was completely eliminated within three weeks. No functionalized SPIONs accumulate in cells by endocytic mechanism, none accumulate in the nucleus, and none are toxic at a desirable concentration. Therefore, they could be used as a dual imaging agent: as contrast agents for MRI and for traditional optical biopsy by using Prussian Blue staining.

Human adenocarcinoma cells of the line WiDr were incubated with 5-aminolevulinic acid to induce protoporphyrin IX (PpIX) and then exposed to laser light of wavelength 635 nm. The PpIX fluorescence decreased with increasing exposure. The decay rate was slightly dependent on the initial PpIX concentration. The PpIX fluorescence was halved by a fluence of about 40 J/cm 2 . Several fluorescing photoproducts were formed. The main one, supposedly the chlorin-type photoprotoporphyrin (Ppp), had a fluorescence excitation spectrum stretching out to about 680 nm with a maximum at around 668 nm. The formation kinetics of this product was dependent on the initial PpIX concentration. Moreover, it was selectively bleached by exposure to light at 670 nm. A photoproduct with an emission maximum at 652 nm, different from Ppp, remained after this exposure. Traces of a photoproduct(s) with fluorescence emission slightly blueshifted compared with that of PpIX, supposedly watersoluble porphyrins, were also detected after light exposure. MATERIALS AND METHODSCell line. WiDr cells, derived from a primary human adenocarcinoma of the rectosigmoid colon, were used (a doubling period about