Perovskite solar cells have emerged as a promising and highly efficient solar technology. Despite efficiencies continuing to climb, the prospect of industrial manufacture is hampered by concerns regarding the safety...
Precious metal (PM) and copper content of dynamic-RAM modules placed on the market during 1991-2008 has been analysed by AAS following comminution and acid digestion. Linear regression analysis of compositional data ordered according to sample chronology was used to identify historic temporal trends in module composition resulting from changes in manufacturing practices, and to project future trends for use in more accurate assessment of future recycling potential. DRAM was found to be 'high grade' waste with: stable levels of gold and silver over time; 80% reduction in palladium content during 1991-2008; and 0.23g/module/year increase in copper content with a 75% projected increase from 2008 by 2020. The accuracy of future recycling potential projections for WEEE using current methods based on static compositional data from current devices is questionable due to likely changes in future device composition. The impact on recycling potential projections of waste laptops, smart phones, cell phones and tablets arising in Europe in 2020 resulting from a 75% increase in copper content is considered against existing projections using static compositional data. The results highlight that failing to consider temporal variations in PM content may result in significant discrepancies between projections and future recycling potential.
For every three people on the planet, there are approximately two Tonnes (Te) of plastic waste. We show that carbon recovery from polystyrene (PS) plastic is enhanced by the coaddition of solvents to grow carbon nanotubes (CNTs) by liquid injection chemical vapour deposition. Polystyrene was loaded up to 4 wt% in toluene and heated to 780 °C in the presence of a ferrocene catalyst and a hydrogen/argon carrier gas at a 1:19 ratio. High resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM), thermogravimetric analysis (TGA) and Raman spectroscopy were used to identify multiwalled carbon nanotubes (MWCNTs). The PS addition in the range from 0 to 4 wt% showed improved quality and CNT homogeneity; Raman “Graphitic/Defective” (G/D) values increased from 1.9 to 2.3; mean CNT diameters increased from 43.0 to 49.2 nm; and maximum CNT yield increased from 11.37% to 14.31%. Since both the CNT diameters and the percentage yield increased following the addition of polystyrene, we conclude that carbon from PS contributes to the carbon within the MWCNTs. The electrical contact resistance of acid-washed Bucky papers produced from each loading ranged from 2.2 to 4.4 Ohm, with no direct correlation to PS loading. Due to this narrow range, materials with different loadings were mixed to create the six wires of an Ethernet cable and tested using iPerf3; the cable achieved up- and down- link speeds of ~99.5 Mbps, i.e., comparable to Cu wire with the same dimensions (~99.5 Mbps). The lifecycle assessment (LCA) of CNT wire production was compared to copper wire production for a use case in a Boeing 747-400 over the lifespan of the aircraft. Due to their lightweight nature, the CNT wires decreased the CO2 footprint by 21 kTonnes (kTe) over the aircraft’s lifespan.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.