No abstract

SBA-15 materials were functionalized with amino groups, APTES. The functionalization was carried out with ethanol or toluene, in air or nitrogen atmosphere. Texture and silanol ratio of functionalized materials were characterized by CO₂ adsorption, N₂ adsorption, SEM, TEM, and NMR. The results of this work indicates that functionalization in toluene is better than functionalization in ethanol, in order to anchor the largest number of APTES molecules on SBA-15 surface. For the same purpose, during functionalization process, the use of nitrogen atmosphere is better than the use of air atmosphere.

No abstract

Carbon microfibers (CMF) has been used as an adsorbent material for CO2 and CH4 capture. The gas adsorption capacity depends on the chemical and morphological structure of CMF. The CMF physicochemical properties change according to the applied stabilization and carbonization temperatures. With the aim of studying the effect of stabilization temperature on the structural properties of the carbon microfibers and their CO2 and CH4 adsorption capacity, four different stabilization temperatures (250, 270, 280, and 300 °C) were explored, maintaining a constant carbonization temperature (900 °C). In materials stabilized at 250 and 270 °C, the cyclization was incomplete, in that, the nitrile groups (triple-bond structure, e.g., C≡N) were not converted to a double-bond structure (e.g., C=N), to form a six-membered cyclic pyridine ring, as a consequence the material stabilized at 300 °C resulting in fragile microfibers; therefore, the most appropriate stabilization temperature was 280 °C. Finally, to corroborate that the specific surface area (microporosity) is not the determining factor that influences the adsorption capacity of the materials, carbonization of polyacrylonitrile microfibers (PANMFs) at five different temperatures (600, 700, 800, 900, and 1000 °C) is carried, maintaining a constant temperature of 280 °C for the stabilization process. As a result, the CMF chemical composition directly affects the CO2 and CH4 adsorption capacity, even more directly than the specific surface area. Thus, the chemical variety can be useful to develop carbon microfibers with a high adsorption capacity and selectivity in materials with a low specific surface area. The amount adsorbed at 25 °C and 1.0 bar oscillate between 2.0 and 2.9 mmol/g adsorbent for CO2 and between 0.8 and 2.0 mmol/g adsorbent for CH4, depending on the calcination treatment applicated; these values are comparable with other material adsorbents of greenhouse gases.

The isosteric enthalpy of adsorption (∆adsh ) of CO2 in three different micro and mesoporous materials was evaluated in this work. These materials were a microporous material with functional groups of nitrogen and oxygen (CMFs, carbon microfibers), a mesoporous material with silanol groups (SBA-15, Santa Barbara Amorphous), and a mesoporous material with amine groups (SBA-15_APTES, SBA-15 amine-functionalized with (3-Aminopropyl)-triethoxysilane). The temperature interval explored was between 263 K and 303 K, with a separation of 5 K between each one, so a total of nine CO2 isotherms were obtained. Using the nine isotherms and the Clausius–Clapeyron equation, the reference value for ∆adsh was found. The reference value was compared with those ∆adsh obtained, considering some arrangement of three or five CO2 isotherms. Finally, it was found that at 298 K and 1 bar, the total amount of CO2 adsorbed is 2.32, 0.53, and 1.37 mmol g−1 for CMF, SBA-15, and SBA-15_APTES, respectively. However, at a coverage of 0.38 mmol g−1, ∆adsh is worth 38, 30, and 29 KJ mol−1 for SBA-15_APTES, CMFs, and SBA-15, respectively. So, physisorption predominates in the case of CMF and SBA-15 materials, and the ∆adsh values significantly coincide regardless of whether the isotherms arrangement used was three or five. Meanwhile, in SBA-15_APTES, chemisorption predominates as a consequence of the arrangements used to obtain . This happens in such a way that the use of low temperatures (263–283 K) tends to produce higher ∆adsh values, while the use of high temperatures (283–303 K) decreases the ∆adsh values.

This work reports a new technique called “Suspension Impregnation Method” (SiM) as an alternative to the “Incipient Impregnation Method” (IiM) for the synthesis of noble metal (Au) nanoparticles. The SiM was used to synthesize gold nanoparticles supported by titanium oxide and compared with those of IiM. The reactor for the SiM technique was based on the principles of mixing, heat, and mass transfer of the suspension reactors and the metal particle synthesis was processed in situ under the oxidation reduction potentials. Three different conditions were established to observe the effect of pH on the size of the metal particles: acid (HCl), neutral (water) and alkaline (urea). The samples were characterized by nitrogen adsorption, X-Ray Diffraction (XRD), Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES), Thermogravimetric Analysis (TGA)/Differential Thermal Analysis (DTA), Transmission Electron Microscopy (TEM) and CO2 adsorption. The surface area was slightly modified, and the average pore diameter was reduced in all materials. The structure of the titanium oxide was not altered. A deposit of organic material was detected in samples synthesized in alkaline medium for both methods. The pH influenced the formation of conglomerates in IiM and resulted in large particle sizes (3–9 nm). In contrast, an in situ reduction in the species in SiM resulted in smaller particle sizes than IiM (2–3 nm).

No abstract

No abstract