In this study, a novel approach of high speed scratching is carried out on silicon (Si) wafers at nanoscale depths of cut to investigate the fundamental mechanisms in wafering of solar cells. The scratching is conducted on a Si wafer of 150 mm diameter with an ultraprecision grinder at a speed of 8.4 to 15 m/s. Single-point diamonds of a tip radius of 174, 324, and 786 nm, respectively, are used in the study. The study finds that at the onset of chip formation, an amorphous layer is formed at the topmost of the residual scratch, followed by the pristine crystalline lattice beneath. This is different from the previous findings in low speed scratching and high speed grinding, in which there is an amorphous layer at the top and a damaged layer underneath. The final width and depth of the residual scratch at the onset of chip formation measured vary from 288 to 316 nm, and from 49 to 62 nm, respectively. High pressure phases are absent from the scratch at the onset of either chip or crack formation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.