The complex, dynamic, and hydrated microstructures of human dentin serve as the major determinant for the restorative performance of biomaterials. This study aimed to evaluate the mechanical properties of human dentin under different hydration conditions. The occlusal dentin of five third molars was exposed and cut into 1 mm2 dentin slabs. The slabs were then polished and further cut into 1 mm2 dentin beams and stored in distilled water. Two beams/tooth were used for testing their hardness (H) and elastic modulus (E) at 5 min (baseline), 1 h, and 24 h after dehydration (23 °C and 30% RH), and also for measuring weight at following dehydration times: 0 min, 5 min, 1 h, and 24 h. Five additional molars were employed to prepare 0.4 mm2 dentin beams (3/tooth) for determining ultimate tensile strength (UTS) at 5 min (baseline), 1 h, and 24 h post-dehydration. Statistical significance was set at α = 0.05. Dehydration time significantly affected H, E, weight-loss, and UTS of dentin (p < 0.05). H and E values showed a strongly positive and significant correlation (r > 0.5, p < 0.05). Dehydration can substantially modify the mechanical properties of dentin, leading to misinterpretation of restorative outcomes in vitro.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.