The efficiency of charge collection at the organic/transparent conducting oxide (TCO) interface in organic photovoltaic (OPV) devices affects overall device efficiency. Modifying the TCO with an electrochemically active molecule may enhance OPV efficiency by providing a charge-transfer pathway between the electrode and the organic active layer, and may also mitigate surface recombination. The synthesis and characterization of phosphonic acid-ruthenium phthalocyanine (RuPcPA) monolayer films on indium tin oxide (ITO), designed to facilitate charge harvesting at ITO electrodes, is presented in this work. The PA group was installed axially relative to the Pc plane so that upon deposition, RuPcPA molecules were preferentially aligned with the ITO surface plane. The tilt angle of 22° between the normal axes to the Pc plane and the ITO surface plane, measured by attenuated total reflectance (ATR) spectroscopy, is consistent with a predominately in-plane orientation. The effect of surface roughness on RuPcPA orientation was modeled, and a correlation was obtained between experimental and theoretical mean tilt angles. Based on electrochemical and spectroelectrochemical studies, RuPcPA monolayers are composed predominately of monomers. Electrochemical impedance spectroscopy (EIS) and potential modulated-ATR (PM-ATR) spectroscopy were used to characterize the electron-transfer (ET) kinetics of these monolayers. A rate constant of 4.0 × 10 s was measured using EIS, consistent with a short tunneling distance between the chromophore and the electrode surface. Using PM-ATR, k values of 2.2 × 10 and 2.4 × 10 s were measured using TE and TM polarized light, respectively; the similarity of these values is consistent with a narrow molecular orientation distribution and narrow range of tunneling distances. The ionization potential of RuPcPA-modified ITO was measured using ultraviolet photoelectron spectroscopy and the results indicate favorable energetics for hole collection at the RuPcPA/ITO interface, indicating that this type of TCO modification may be useful for enhancing charge collection efficiency in OPV devices.

Conduction and valence band energies (ECB, EVB) for CdSe nanorods (NRs) functionalized with Au nanoparticle (NP) tips are reported here, referenced to the vacuum scale. We use (a) UV photoemission spectroscopy (UPS) to measure EVB for NR films, utilizing advanced approaches to secondary electron background correction, satellite removal to enhance spectral contrast, and correction for shifts in local vacuum levels; and (b) waveguide-based spectroelectrochemistry to measure ECB from onset potentials for electron injection into NR films tethered to ITO. For untipped CdSe NRs, both approaches show EVB = 5.9-6.1 eV and ECB = 4.1-4.3 eV. Addition of Au tips alters the NR band edge energies and introduces midgap states, in ways that are predicted to influence the efficiency of these nanomaterials as photoelectrocatalysts. UPS results show that Au tipping shifts EVB closer to vacuum by up to 0.4 eV, shifts the apparent Fermi energy toward the middle of the band gap, and introduces additional states above EVB. Spectroelectrochemical results confirm these trends: Au tipping shifts ECB closer to vacuum, by 0.4-0.6 eV, and introduces midgap states below ECB, which are assigned as metal-semiconductor interface (MSI) states. Characterization of these band edge energies and understanding the origins of MSI states is needed to design energy conversion systems with proper band alignment between the light absorbing NR, the NP catalyst, and solution electron donors and acceptors. The complementary characterization protocols presented here should be applicable to a wide variety of thin films of heterogeneous photoactive nanomaterials, aiding in the identification of the most promising material combinations for photoelectrochemical energy conversion.

This report focuses on the evaluation of the electrochemical properties of both solution-deposited sol-gel (sg-ZnO) and sputtered (sp-ZnO) zinc oxide thin films, intended for use as electron-collecting interlayers in organic solar cells (OPVs). In the electrochemical studies (voltammetric and impedance studies), we used indium-tin oxide (ITO) over coated with either sg-ZnO or sp-ZnO interlayers, in contact with either plain electrolyte solutions, or solutions with probe redox couples. The electroactive area of exposed ITO under the ZnO interlayer was estimated by characterizing the electrochemical response of just the oxide interlayer and the charge transfer resistance from solutions with the probe redox couples. Compared to bare ITO, the effective electroactive area of ITO under sg-ZnO films was ca. 70%, 10%, and 0.3% for 40, 80, and 120 nm sg-ZnO films. More compact sp-ZnO films required only 30 nm thicknesses to achieve an effective electroactive ITO area of ca. 0.02%. We also examined the electrochemical responses of these same ITO/ZnO heterojunctions overcoated with device thickness pure poly(3-hexylthiophehe) (P3HT), and donor/acceptor blended active layers (P3HT:PCBM). Voltammetric oxidation/reduction of pure P3HT thin films on ZnO/ITO contacts showed that pinhole pathways exist in ZnO films that permit dark oxidation (ITO hole injection into P3HT). In P3HT:PCBM active layers, however, the electrochemical activity for P3HT oxidation is greatly attenuated, suggesting PCBM enrichment near the ZnO interface, effectively blocking P3HT interaction with the ITO contact. The shunt resistance, obtained from dark current-voltage behavior in full P3HT/PCBM OPVs, was dependent on both (i) the porosity of the sg-ZnO or sp-ZnO films (as revealed by probe molecule electrochemistry) and (ii) the apparent enrichment of PCBM at ZnO/P3HT:PCBM interfaces, both effects conveniently revealed by electrochemical characterization. We anticipate that these approaches will be applicable to a wider array of solution-processed interlayers for "printable" solar cells.

Efficient charge harvesting at electrodes is critical for the effective performance of organic photovoltaics and is strongly influenced by the first molecular monolayer at the transparent conducting oxide electrode. Herein, we present a study of the relationship between molecular orientation and tunneling distance on charge-transfer rates between a tethered sub-monolayer/monolayer of phosphonic acid (PA)-functionalized Zn phthalocyanines (ZnPcs) and an indium tin oxide (ITO) surface by a combination of electrochemical techniques and waveguide tools such as attenuated total reflectance (ATR) UV–vis spectroscopy and potential-modulated ATR (PM-ATR) spectroelectrochemistry. The distance between the main chromophore and PA anchoring group was modulated by an aliphatic carbon of various lengths (n = 3, 9, 10, or 11) that resulted in an extended distance of 7–18 Å between the ZnPcs and the ITO surface. Modified ITO surfaces were composed of monomeric and aggregated subpopulations of ZnPcs with molecular orientations predominantly in-plane (36–39°) and out-of-plane (72–75°), respectively. Charge-transfer rate constants (k s,opt) were measured using PM-ATR. For a given tether length, the aggregated subpopulations exhibit higher k s,opt values compared to the monomeric subpopulations. The observed k s,opt values had an exponential dependence on the effective tunneling distance with a decay constant (β) that ranged from 0.32 to 0.47 Å–1, depending on the chromophore orientation and aggregation state. The fastest charge-transfer rate constants were found for the chromophores with the smallest tunneling distance (n = 3). A k s,opt of 3.9 × 104 s–1 represents the fastest rate constant measured by PM-ATR for a PA-functionalized ZnPc chromophore tethered to an ITO waveguide electrode.