No abstract

We report the design, synthesis and photoelectrochemical characterization of cobalt phosphate (Co-Pi) oxygen evolution catalyst modified heterojunction photoelectrodes consisting of one-dimensional WO3 nanorods (1D-WO3) and highly porous BiVO4 layers. The 1D-WO3 nanorods were prepared by the decomposition of the tetrabutylammonium decatungstate precursor in the presence of poly(ethylene glycol) as a binding agent. The porous BiVO4 layers were spray deposited using a surfactant assisted metal-organic decomposition method. The Co-Pi oxygen evolution catalyst was deposited onto the BiVO4/1D-WO3/FTO heterojunction electrode using a photoassisted electrodeposition method. The Co-Pi catalyst modified heterojunction electrodes exhibited a sustained enhancement in the photocurrent compared to the unmodified BiVO4/1D-WO3/FTO heterojunction electrodes. The improved photoelectrochemical properties profited from the enhanced charge carrier separation achieved through the integration of highly porous BiVO4 layers on top of 1D-WO3 nanorods and from the superior kinetics due to the presence of the Co-Pi oxygen evolution catalyst on top of BiVO4/1D-WO3/FTO heterojunction electrodes.

No abstract

An alkaline exchange membrane (AEM) based on an aminated trimethyl poly(phenylene) is studied in detail. This article reports hydroxide ion conductivity through an in situ method that allows for a more accurate measurement. The ionic conductivities of the membrane in bromide and carbonate forms at 90 °C and 95% RH are found to be 13 and 17 mS cm−1 respectively. When exchanged with hydroxide, conductivity improved to 86 mS cm−1 under the same experimental conditions. The effect of relative humidity on water uptake and the SAXS patterns of the AEM membranes were investigated. SAXS analysis revealed a rigid aromatic structure of the AEM membrane with no microphase separation. The synthesized AEM is shown to be mechanically stable as seen from the water uptake and SAXS studies. Diffusion NMR studies demonstrated a steady state long‐range diffusion constant, D∞ of 9.8 × 10−6 cm2 s−1 after 50–100 ms. © 2012 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2013, 51, 1743–1750, 2013

Tungsten trioxide nanorods have been generated by the thermal decomposition (450 °C) of tetrabutylammonium decatungstate. The synthesized tungsten trioxide (WO3) nanorods have been characterized by XRD, Raman, SEM, TEM, HRTEM and cyclic voltammetry. High resolution transmission electron microscopy and X-ray diffraction analysis showed that the synthesized WO3nanorods are crystalline in nature with monoclinic structure. The electrochemical experiments showed that they constitute a better electrocatalytic system for hydrogen evolution reaction in acid medium compared to their bulk counterpart.