The effects of addition of reinforcing carbon nanotubes (CNTs) into hydrogenated nitrile-butadiene rubber (HNBR) matrix on the mechanical, dynamic viscoelastic, and permeability properties were studied in this investigation. Different techniques of incorporating nanotubes in HNBR were investigated in this research. The techniques considered were more suitable for industrial preparation of rubber composites. The nanotubes were modified with different surfactants and dispersion agents to improve the compatibility and adhesion of nanotubes on the HNBR matrix. The effects of the surface modification of the nanotubes on various properties were examined in detail. The amount of CNTs was varied from 2.5 to 10 phr in different formulations prepared to identify the optimum CNT levels. A detailed analysis was made to investigate the morphological structure and mechanical behavior at room temperature. The viscoelastic behavior of the nanotube filler elastomer was studied by dynamic mechanical thermal analysis (DMTA). Morphological analysis indicated a very good dispersion of the CNTs for a low nanotube loading of 3.5 phr. A significant improvement in the mechanical properties was observed with the addition of nanotubes. DMTA studies revealed an increase in the storage modulus and a reduction in the glass-transition temperature after the incorporation of the nanotubes. Further, the HNBR/CNT nanocomposites were subjected to permeability studies. The studies showed a significant reduction in the permeability of nitrogen gas.
In this research, two different methods have been investigated for optimising the preparation of hydrogenated acrylonitrile butadiene rubber/clay nanocomposites. Commercially available organoclay (Cloisite 20A) has been considered for the preparation of rubber nanocomposites. A detailed analysis has been made to investigate the morphological structure and mechanical behaviour at room temperature and at elevated temperature. Also the influence of organoclays on permeability has been studied. Structural analysis indicates very good dispersion for a low loading of 5 parts per hundred (phr) amount of nanoclays. Significant improvements in mechanical properties have been observed with the addition of organoclays at both room and elevated temperatures. Even with the low level of addition of nanoclays, there was a remarkable reduction in permeability.
Hydrogenated nitrile butadiene rubber (HNBR) nanocomposites were prepared using commercially available organoclays (Cloisite 15A). The main focus of the current investigation is to study the influence of the organoclay reinforced in HNBR after subjecting it to long-term oxidative ageing and immersion studies. All the different nanoclay nanocomposites were air aged for a period of 168 h and at 150°C. The changes in the mechanical properties such as tensile strength and elongation at break have been compared with respect to the control sample. For immersion tests, three different liquid mediums were considered for this current investigation. All the samples were immersed in different mediums for a period of 168 h at 150°C. The changes in the swelling index and the mechanical properties have been reported with respect to the control sample. After reinforcing nanoclays into HNBR there was good resistance to swelling in all the three different liquid mediums in comparison to control sample. Tensile testing was performed on the immersed nanocomposites to evaluate the mechanical behaviour after immersion studies. A probable mechanism behind the improved performance has been suggested.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.