Interfacial adhesion of basalt and glass fibre reinforced polypropylene composites was studied using microdebond testing technique. A focus was put on a simple approach of applying extruded thermoplastic films as a matrix material for microdroplet formation. The ability of different viscosity and thickness polypropylene films to form symmetrical droplets under a temperature range of 200–240℃ was evaluated. Emphasis was put on polypropylene matrix chemistry, silane fibre surface treatment and testing loading rate impact on interfacial performance change in polypropylene-basalt fibre and polypropylene-glass fibre microcomposites. It was found that it was possible to obtain high symmetrical droplet yield out of polypropylene films of melt flow rate 50 and 125 g/10 min and 55–85 µm thickness at 240℃. The presence of maleic anhydride grafted polypropylene coupling agent increased the interfacial shear strength significantly. Microcomposites with glass fibre had higher interfacial shear strength in comparison with the used basalt fibre, mainly due to the difference in their sizing. Various silane-based fibre surface coatings did not result in significant interfacial adhesion changes. Polypropylene-glass fibre microcomposite interfacial shear strength at 0.5, 3.0 and 10.0 mm min–1 loading rates had similar values with high maximum pull-out force scatter at 0.5 and 3.0 mm min–1 loading rates and low scatter at 10.0 mm min–1.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.