The diffusion of phosphorus from a thick epitaxial layer into a silicon substrate has been investigated using the spreading-resistance technique. By comparing the diffusion profile under a free oxidized surface with the profile under a masked surface, it has been shown that surface oxidation enhances diffusion at low temperatures and retards diffusion at high temperatures. The conditions which favor enhanced diffusion are those under which stacking faults grow; retarded diffusion is associated with stacking-fault shrinkage. Enhanced diffusion is due to the oxide injecting excess interstitials into the substrate; retarded diffusion is caused by vacancy injection. It is concluded that phosphorus diffuses by the interstitialcy mechanism and that the criterion for interstitial or vacancy injection is the relative value of the anion and cation fluxes across the oxide-silicon interface.
The electrical conductivity of high purity (99.8 pct) A1N has been determined using both a-c and d-c techniques. Measurements were made at temperatures between 700 ~ and 1000~C and in a nitrogen pressure range of 1-10 -5 atm. The electrical conductivity is independent of nitrogen pressure. Galvanic cell results indicate that ionic conduction is negligible. Over the experimental temperature range, the electrical conductivity of A1N follows the equation ,7(ohm-l-cm -~) = 6.89 • 103 exp (--E/kT) where the activation energy (E) is 1.82 • 0.06 eV. It is concluded that the conduction process is extrinsic due to carbon impurities (,,,350 ppm) present in the A1N.Aluminum nitride is a potentially useful refractory material, particularly at elevated temperatures. Its oxidation in air at temperatures up to 600~ is low (1, 2), and it is resistant to attack by acids, molten metals, and water vapor (1, 3). Recent studies indicate that A1N is very resistant to chemical attack by lithium at 400~ (4); thus A1N may be a suitable electronic insulator in alkali metal-molten salt batteries. Aluminum nitride also has potential applications in elevated temperature semiconductor devices (5-7). Although these various applications require a detailed knowledge of its conductivity at elevated temperatures, there is considerable variation in the activation energy and magnitude of the electrical conductivity of A1N measured by previous investigators (1,3,6,(8)(9)(10)(11)(12). In this study the electrical conductivity of high purity (>99%) A1N has been measured using a-c and d-c techniques at temperatures between 700 ~ and 1000~ and at nitrogen pressures between 1 and 10 -5 atm. ExperimentalHot-pressed polycrystalline A1N samples were prepared by Cerac/Pure Incorporated. Aluminum nitride powder was synthesized by the electric discharge method (3) and hot-pressed without binder in a graphite die at ~1600~ under a nitrogen atmosphere. The 1 cm diameter A1N rod was machined to remove surface-impregnated carbon and then cut into pellets of different thicknesses. Sample porosity did not exceed 5%. The pellets were annealed in our laboratory at 1400~ for 76 hr in high purity nitrogen. Chemical analyses performed by the supplier both before and after annealing are listed in Table I. It should be emphasized that the purity of the annealed samples (99.8%) is higher than A1N samples used in previous studies.Gold electrical contacts, which were used in the a-c conductivity measurements, were fabricated using the following procedure. The fiat surfaces of the AIN pellets were polished and then rinsed in acetone and petroleum ether. After coating the fiat surfaces with du Pont thermosetting gold paste (No. 5780), the pellets were heated slowly in air to 200~ held for 10 hr, and then annealed for 2 hr at 400~ Coherent gold contacts with less than 0.1 ohm resistance across 9 Electrochemical Society Active Member. Key words: extrinsic conduction in A1N', effect of carbon impurities, electronic conductivity in A1N, chromium nitride electrodes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.