ZnFe 2 O 4 particles ranging from 4 to 19 nm have been prepared by a solvothermal method. They exhibit superparamagnetic behavior above the blocking temperature which takes a value from 14 to 62 K, magnetization values from 30 to 60 emu g À1 , an anisotropy constant that ranges from 1.1 Â 10 5 to 3.4 Â 10 5 erg cm À3 and an effective superparamagnetic moment from 7.0 Â 10 2 to 8.6 Â 10 3 m B . The superparamagnetic behavior is affected by the presence of dipolar interparticle interactions which are deeply influenced by the synthesis conditions. These interactions yield a wider ZFC maximum and a higher blocking temperature. Moreover, other kinds of interparticle interactions have been found to take place at low temperature and occur through frozen surface spins. Whereas the dipole interactions reduce the anisotropy of the system, the surface spin interactions tend to increase it and the material becomes magnetically harder.
ZnFe 2 O 4 nanoparticles with sizes between 3 and 20 nm have been prepared nonembedded and embedded in an amorphous SiO 2 matrix. All the samples are ferrimagnetic below the blocking temperature that presents similar values for all of them, indicated by the maxima in the ZFC/FC curves. However, the embedded nanoparticles with sizes between 3 and 7 nm present much higher values of coercive field than the nonembedded particles. The fact that particles with different sizes present similar blocking temperature values suggests that they have similar anisotropy energy, and this has been justified using experimental anisotropy constants determined for different sized nanoparticles. Although the matrix can increase the surface anisotropy of the particles, it would not greatly affect the core anisotropy. Taking this into account, it can be justified that embedded particles present a higher coercive field but similar blocking temperature than nonembedded particles. From the variation of the coercive field as a function of the particle size, the limit between the single-domain and multidomain regions seems to be in the range of 15-18 nm. The range of temperature in which the samples behave as superparamagnetic has been estimated from the plots of the inverse susceptibility versus temperature. The particle size and the inversion parameter control the magnetization value that seems to determine the transition temperature from superparamagnetic to paramagnetic behavior.
Two
kinds of nanosized ferrite systems have been prepared: MFe2O4 nanoparticles and MFe2O4/SiO2 (M: Co, Ni) nanocomposites with different
ferrite particle sizes. Magnetic measurements have been done for both
ferrite systems in the 5–700 K temperature range, and the silica
matrix effect on the magnetic behavior has been studied. Whereas CoFe2O4 samples are characterized by high anisotropy
values, NiFe2O4 particles seem to be magnetically
soft, which may favor the dipolar interactions. The silica matrix
avoids all kinds of particle interactions that modify the magnetic
behavior. Therefore, in 2–5 nm embedded Co-ferrite particles,
a decreasing H
C value with the increasing
particle size is not observed. This almost constant H
C value indicates that interactions between surface spins
of different particles are absent for this particle size range. In
the case of Ni-ferrite particles, the dipolar interactions between
bulk particle moments are minimized due to the presence of the SiO2 matrix.
Cation ordering in ABO3 perovskites adds to their chemical variety and can lead to properties such as ferrimagnetism and magnetoresistance in Sr2 FeMoO6 . Through high-pressure and high-temperature synthesis, a new type of "double double perovskite" structure has been discovered in the family MnRMnSbO6 (R=La, Pr, Nd, Sm). This tetragonal structure has a 1:1 order of cations on both A and B sites, with A-site Mn(2+) and R(3+) cations ordered in columns and Mn(2+) and Sb(5+) having rock salt order on the B sites. The MnRMnSbO6 double double perovskites are ferrimagnetic at low temperatures with additional spin-reorientation transitions. The ordering direction of ferrimagnetic Mn spins in MnNdMnSbO6 changes from parallel to [001] below TC =76 K to perpendicular below the reorientation transition at 42 K at which Nd moments also order. Smaller rare earths lead to conventional monoclinic double perovskites (MnR)MnSbO6 for Eu and Gd.
The perovskite polymorph of Mn(2)CrSbO(6) compound has been synthesized at 8 GPa and 1473 K. It crystallizes in the monoclinic P21/n space group with cell parameters a = 5.2180 (2) Å, b = 5.3710(2) Å, c = 7.5874(1) Å and β = 90.36(1)°. Magnetic susceptibility and magnetization measurements show the simultaneous antiferromagnetic ordering of Mn(2+) and Cr(3+) sublattices below TN = 55 K with a small canting. Low temperature powder neutron diffraction reveals a commensurate magnetic structure with spins confined to the ac-plane and a propagation vector κ = [1/2 0 1/2]. The thermal treatment of this compound induces an irreversible phase transition to the ilmenite polymorph, which has been isolated at 973 K and crystallizes in R3[combining macron] space group with cell parameters a = 5.2084 (4) Å and c = 14.4000 (11) Å. Magnetic susceptibility, magnetization and powder neutron diffraction data confirm the antiferromagnetic helical ordering of spins in an incommensurate magnetic structure with κ = [00 0.46] below 60 K, and the temperature dependence of the propagation vector up to κ = [00 0.54] at about 10 K.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.