Compatibility of natural rubber (NR)/polystyrene (PS) blend is poor and can be enhanced by the addition of a graft copolymer of natural rubber and polystyrene (NR-graft-PS). The effects of homopolymer molecular weight, copolymer molecular weight, copolymer concentration, processing conditions and mode of addition on the morphology of the dispersed phase have been investigated by means of optical microscopy. The addition of a small percentage of the compatibilizer decreases the domain size of the dispersed phase. The effect levels off at higher concentrations. The leveling off could be an indication of interfacial saturation. The experimental results were compared with the theoretical predictions of Noolandi and Hong. The addition of the graft copolymer improves the mechanical properties of the blend and attempts were made to correlate the mechanical properties with the morphology of the system. Attempts were also made to understand the conformation of the graft copolymer at the interface.
Blends of natural rubber (NR) and polystyrene (PS) were prepared by melt mixing in a Brabender plasticorder and by solution casting using chloroform as the casting solvent. Earlier studies have indicated that these blends are incompatible and immiscible, and their compatibility can be improved by the addition of a graft copolymer of NR and PS (NR-g-PS). The rheological behavior of these blends has been carried out in the presence and absence of the compatibilizer using a capillary rheometer and a melt flow indexer. The effects of blend ratio, processing techniques (melt mixing versus solution casting), shear stress, and temperature on the rheological behavior have been studied in detail. Both in the presence and absence of the copolymer, the blends showed a decrease in viscosity with an increase of shear stress, indicating pseudoplastic nature. Solution-cast blends showed a higher viscosity as compared to melt-mixed blends. The viscosity versus composition curve of both melt-mixed and solution-cast blends showed negative deviation from the additivity at a higher shear rate region. This is associated with the interlayer slip between the highly incompatible NR and PS phases. The effects of graft copolymer loading and temperature on solution-cast blends were studied, and it was found that as the copolymer loading increases, the shear viscosity increases. This is due to the high interfacial interaction between the two components in the presence of the copolymer. The copolymer, in fact, locates at the interface and makes the interface more broad. However, at higher loading of the copolymer, the viscosity of the blends decreases. This may be associated with the formation of micelles, which have a plasticizing action on the viscosity of the blends. Melt elasticity parameters like principal normal stress difference, recoverable elastic shear strain, and die swell were evaluated. Master curves have been generated using modified viscosity and shear rate functions that contain the melt flow index as a parameter. The extrudate morphology of the blends was studied using a scanning electron microscope. Addition of the copolymer reduces the domain size of the dispersed phase, followed by a leveling off at a higher concentration. The leveling off is an indication of interfacial saturation. The interparticle distance also decreased followed by a leveling off at a higher loading of the copolymer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.