This work reports results of a study carried out to optimize the preparation conditions of Cu 2 ZnSnS 4 (CZTS) thin films grown by sequential deposition of Cu 2 SnS 3 (CTS) and ZnS layers, where the Cu 2 SnS 3 compound was grown using a novel procedure consisting of simultaneous precipitation of Cu 2 S and SnS 2 performed by diffusion membrane assisted chemical bath deposition (CBD) technique. The precipitation across the diffusion membranes allows achieving moderate control of release of metal ions into the work solution favoring the heterogeneous growth mainly through an ion-ion mechanism. Through a parameters study, conditions were found to grow Cu 2 SnS 3 thin films which were used as precursors for the formation of Cu 2 ZnSnS 4 films. The formation of CZTS thin films grown in the Cu 2 ZnSnS 4 phase was verified through measurements of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy. Solar cells with efficiencies of 4.9% were obtained using CZTS films prepared by membrane assisted CBD technique as absorber layer.
Solar cells based on kesterite-type Cu2ZnSnS4 (CZTS) thin films were fabricated using a chemical route to prepare the CZTS films, consisting in sequential deposition of Cu2SnS3 (CTS) and ZnS thin films followed by annealing at 550 • C in nitrogen atmosphere. The CTS compound was prepared in a one-step process using a novel chemical procedure consisting of simultaneous precipitation of Cu2S and SnS2 performed by diffusion membranes assisted CBD (chemical bath deposition) technique. Diffusion membranes were used to optimize the kinetic growth through a moderate control of release of metal ions into the work solution. As the conditions for the formation in one step of the Cu2SnS3 compound have not yet been reported in literature, special emphasis was put on finding the parameters that allow growing the Cu2SnS3 thin films by simultaneous precipitation of Cu2S and SnS2. For that, we propose a methodology that includes numerical solution of the equilibrium equations that were established through a study of the chemical equilibrium of the system SnCl2, Na3C6H5O7·2H2O, CuCl2 and Na2S2O3·5H2O. The formation of thin films of CTS and CZTS free of secondary phases grown with a stoichiometry close to that corresponding to the Cu2SnS3 and Cu2ZnSnS4 phases, was verified through measurements of X-ray diffraction (XRD) and Raman spectroscopy. Solar cell with an efficiency of 4.2%, short circuit current of 16.2 mA/cm 2 and open-circuit voltage of 0.49 V was obtained.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.